Aluminum 5005 vs 5086
Aluminum · grade comparison
Aluminum 5005 and 5086 are both aluminum grades. 5086 is the stronger of the two: yield strength 207 MPa (30 ksi) against 138 MPa (20 ksi) for 5005, about 50% more; tensile strength follows at 290 MPa (42.1 ksi) vs 159 MPa (23.1 ksi). 5086 is the more ductile: elongation 12% versus 8% for 5005, and 5086 is harder (75 HB vs 41 HB). 5005 runs hotter in service (120°C vs 65°C continuous) and 5005 conducts heat better (200 W/m·K vs 125 W/m·K). On the shop floor, 5005 sits in a lower cost tier (budget, $) than 5086 (standard, $$).
5005Choose it when the part sees heat, or when cost is the deciding factor.
5086Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
5005 vs 5086: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Bulk Modulus 69 GPa10 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.8 µm/m·K13.2 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Machinability 45 / 100 · Weldability 88 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 35%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 5005 | 5086 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | 0.5 mm | 0.5 mm |
| Best machined surface | Ra 0.8 µm | Ra 0.8 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 16 finishes: Anodizing Type II, Cerakote, Chem Film (Alodine), DLC, E-Coating, Electroless Nickel (EN), Electropolishing, Epoxy Coating, Gold Plating, Hard Anodize Type III w/ PTFE, Hard Anodizing Type III, Nickel Plating and 4 more.
5005 vs 5086 — frequently asked
Is 5086 stronger than 5005?
Yes. 5086 has a typical yield strength of 207 MPa (30 ksi) against 138 MPa (20 ksi) for 5005 — about 50% more. Tensile strength is 290 MPa (42.1 ksi) vs 159 MPa (23.1 ksi).
Which is cheaper, 5005 or 5086?
5005 is the lower-cost material: it sits in the budget tier ($) while 5086 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
When should I choose 5005 over 5086?
Pick 5005 when the part sees heat, or when cost is the deciding factor. Pick 5086 when strength drives the design, or when the part is bent, formed or impact-loaded.