YW2 SINT
Print state · default condition
ISO M20
SINT = sintered
Use the conventional vacuum liquid-phase sintered blank or insert for general rough and semi-finish turning where cost matters more than peak edge strength.
Values for the SINT condition
Other YW2 tempers and conditions
YW2 is listed in 2 conditions; see the grade overview at YW2.
- SINT
- HIP
Compare all 2 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
SINTDefaultThis page Sintered | Use the conventional vacuum liquid-phase sintered blank or insert for general rough and semi-finish turning where cost matters more than peak edge strength. | — | 1,000 | 0 | 1,450 HV | 30 W/m·K |
Hot isostatic pressed | Choose low-pressure sinter-HIP when porosity must be eliminated for higher transverse rupture strength and toughness in interrupted cutting and heavy roughing. | — | 1,100 | 0 | 1,470 HV | 31 W/m·K |
What is YW2 SINT?
YW2 SINT is YW2 in the SINT condition — use the conventional vacuum liquid-phase sintered blank or insert for general rough and semi-finish turning where cost matters more than peak edge strength. YW2 SINT has a tensile strength of 1,000 MPa (145 ksi), stronger than 85% of ceramic grades. Elongation at break is 0% and the elastic modulus is 540 GPa (78.3 Msi). YW2 SINT has a density of 13 g/cm³ (0.47 lb/in³), heavier than 86% of ceramic grades. It melts at 1,320°C (2,408 °F).
Advantages
- Tough — resists crack growth — 10.5 MPa·√m (9.56 ksi·√in), better than 89% of ceramic grades
- Stiff — 540 GPa (78.3 Msi), better than 86% of ceramic grades
Limitations
- High embodied carbon — 30 kg CO₂/kg, worse than 91% of ceramic grades
- Heavy — 13 g/cm³ (0.47 lb/in³), worse than 86% of ceramic grades
- Needs corrosion protection — 50/100, worse than 83% of ceramic grades
YW2 SINT properties
Typical room-temperature values for YW2 SINT; 14 are specific to this condition. Other listed values are YW2 reference data and may not represent this condition. Bars are the position among ceramic grades.
Physical3
YW2 SINT has a density of 13 g/cm³ (0.47 lb/in³), heavier than 86% of ceramic grades. It melts at 1,320°C (2,408 °F).
Mechanical13
YW2 SINT has a tensile strength of 1,000 MPa (145 ksi), stronger than 85% of ceramic grades. Elongation at break is 0% and the elastic modulus is 540 GPa (78.3 Msi).
Thermal5
YW2 SINT is rated for continuous service to 900°C (1,652 °F). It conducts heat at 30 W/m·K (17.3 BTU/hr·ft·°F), better than 60% of ceramic grades. Thermal expansion is 6.2 µm/m·K (3.44 µin/in·°F).
Electrical2
YW2 SINT has an electrical resistivity of 3.5×10⁻⁷ Ω·m.
Chemical & Environmental2
Corrosion resistance is fair (50/100), worse than 83% of ceramic grades.
Sustainability4
Producing a kilogram of YW2 SINT takes about 400 MJ of energy and emits 30 kg of CO₂ — more than 88% of ceramic grades. Typical recycled content is 25%.
Manufacturability3
YW2 SINT's machinability is not recommended (5/100, worse than 59% of ceramic grades).
Common Calculations4
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with YW2 SINT
Is YW2 easy to machine?
Diamond-wheel grinding, EDM or laser only; conventional turning and milling are not possible. Flood cool during grinding to prevent thermal cracking.
Can YW2 be welded?
Not fusion weldable. Inserts and tips are vacuum or induction brazed to steel bodies with silver-based (BAg-type) filler, then cooled slowly to limit residual stress.
Can YW2 be formed, bent or molded?
Powder blending, pressing or extrusion, dewaxing, then vacuum or low-pressure HIP liquid-phase sintering; linear shrinkage is about 18-20 %, so tooling must be sized to the shrink factor.
What surface finishes work on YW2?
Diamond grinding and polishing give mirror cutting edges. CVD (TiN/TiCN/Al2O3) or PVD (TiAlN) coatings can be applied, and blast honing of the edge improves chipping resistance.
YW2 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Cobinder phase | 7.5 – 8.5 | 8 |
| TiCcrater wear resistance | 5 – 7 | 6 |
| TaC+NbCrefines grain, raises high-temperature strength | 3 – 5 | 4 |
| WCbalance; grain size about 1–3 µm | balance | — |
YW2 SINT — frequently asked
What is YW2 SINT used for?
YW2 SINT is typically used for stainless steel roughing, heat-resistant alloy machining and general lathe/mill tooling. In short: tougher universal grade; roughing to semi-finishing; handles interrupted cuts.
What is the tensile strength of YW2 SINT?
YW2 SINT has a typical tensile strength of 1,000 MPa (145 ksi) — stronger than 85% of ceramic grades. Strength varies by condition: see the 2 listed tempers.
Is YW2 SINT easy to machine?
Not especially — machinability is rated not recommended (5/100, worse than 59% of ceramic grades). Diamond-wheel grinding, EDM or laser only; conventional turning and milling are not possible. Flood cool during grinding to prevent thermal cracking.
Can YW2 SINT be welded?
Not fusion weldable. Inserts and tips are vacuum or induction brazed to steel bodies with silver-based (BAg-type) filler, then cooled slowly to limit residual stress.
What surface finishes work on YW2 SINT?
Diamond grinding and polishing give mirror cutting edges. CVD (TiN/TiCN/Al2O3) or PVD (TiAlN) coatings can be applied, and blast honing of the edge improves chipping resistance.
Can YW2 SINT be formed, bent or molded?
Powder blending, pressing or extrusion, dewaxing, then vacuum or low-pressure HIP liquid-phase sintering; linear shrinkage is about 18-20 %, so tooling must be sized to the shrink factor.
What is the maximum service temperature of YW2 SINT?
YW2 SINT is rated for continuous use to about 900°C (1,652 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- ASM Handbook Vol.2 — Cemented Carbides — ASM International (1990)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.