TiB2 HIP (Hot isostatic pressed)
Print state
Pick hot isostatic pressing at ≥99 % purity and >99.5 % density for the highest strength and lowest porosity — armour panels and complex, highly stressed wear parts.
Values for the HIP condition
Other TiB2 tempers and conditions
TiB2 is listed in 6 conditions; see the grade overview at TiB2.
Compare all 6 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
TiB₂–AlN | Use the AlN(–BN) evaporation-boat formulation for vacuum aluminium metallising: resistive heating, resistance to molten-aluminium wetting and better thermal shock resistance than the plain boride. | — | 65 | 0.07 | 900 HV | 60 W/m·K |
TiB₂–SiC | Choose the 10–30 vol % SiC particulate addition to refine grain size and raise strength and oxidation resistance for armour and high-temperature wear parts. | — | 350 | 0.12 | 2,800 HV | 80 W/m·K |
TiB₂–BN | Use the hexagonal BN addition when the part must be turned and milled directly with carbide tooling — continuous-casting break rings and molten-metal sizing components. | — | — | — | 600 HV | 45 W/m·K |
Pressureless sintered TiB₂ with sintering aids | Choose pressureless sintering with aids at 95–97 % density for large or complex parts such as aluminium reduction cell cathode blocks, accepting slightly lower strength and hardness. | — | — | — | 2,500 HV | 70 W/m·K |
HPDefault Hot-pressed TiB₂, ≥98 % purity, ~99 % dense | Default fully dense grade at ≥98 % purity and about 99 % density for wear parts, wire-drawing dies, molten-aluminium contact components and electrodes. | — | — | — | 3,000 HV | 90 W/m·K |
HIPThis page Hot isostatic pressed | Pick hot isostatic pressing at ≥99 % purity and >99.5 % density for the highest strength and lowest porosity — armour panels and complex, highly stressed wear parts. | — | — | — | 3,300 HV | 100 W/m·K |
What is TiB2 HIP?
TiB2 HIP is TiB2 in the HIP condition — pick hot isostatic pressing at ≥99 % purity and >99.5 % density for the highest strength and lowest porosity — armour panels and complex, highly stressed wear parts. The elastic modulus is 565 GPa (81.9 Msi). TiB2 HIP has a density of 4.52 g/cm³ (0.163 lb/in³), lighter than 54% of ceramic grades. It melts at 3,225°C (5,837 °F). HP is the default condition FabDigit quotes; HIP is available on request or by drawing note.
Advantages
- Stiff — 565 GPa (81.9 Msi), better than 89% of ceramic grades
- Conducts heat well — 100 W/m·K (57.8 BTU/hr·ft·°F), better than 83% of ceramic grades
Limitations
- High embodied carbon — 25 kg CO₂/kg, worse than 78% of ceramic grades
TiB2 HIP properties
Typical room-temperature values for TiB2 HIP; 12 are specific to this condition. Other listed values are TiB2 reference data and may not represent this condition. Bars are the position among ceramic grades.
Physical3
TiB2 HIP has a density of 4.52 g/cm³ (0.163 lb/in³), lighter than 54% of ceramic grades. It melts at 3,225°C (5,837 °F).
Mechanical10
The elastic modulus is 565 GPa (81.9 Msi).
Thermal5
TiB2 HIP is rated for continuous service to 950°C (1,742 °F). It conducts heat at 100 W/m·K (57.8 BTU/hr·ft·°F), better than 83% of ceramic grades. Thermal expansion is 6.6 µm/m·K (3.67 µin/in·°F).
Electrical2
TiB2 HIP has an electrical resistivity of 1.5×10⁻⁷ Ω·m.
Chemical & Environmental2
Corrosion resistance is very good (70/100), worse than 59% of ceramic grades.
Sustainability3
Producing a kilogram of TiB2 HIP takes about 350 MJ of energy and emits 25 kg of CO₂ — more than 81% of ceramic grades. Typical recycled content is 0%.
Manufacturability3
TiB2 HIP's machinability is not recommended (5/100, worse than 59% of ceramic grades).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with TiB2 HIP
Is TiB2 easy to machine?
After sintering only diamond grinding and lapping apply, but the low electrical resistivity allows wire and sinker EDM — the main machining advantage of TiB₂ over other ultra-hard ceramics.
Can TiB2 be welded?
Not fusion weldable; join to metals by active brazing with Ti- or Zr-bearing fillers, or by mechanical clamping. Match thermal expansion to avoid cracking.
Can TiB2 be formed, bent or molded?
Near-net shape comes from cold isostatic pressing of powder plus pressureless sintering, or hot pressing in graphite dies at 1800–2000 °C and 20–30 MPa; HIP is used for fully dense complex parts.
What surface finishes work on TiB2?
Diamond lapping and polishing reach Ra < 0.1 µm. No plating or painting; SiC or oxide coatings can be added to suppress oxidation above 900 °C.
TiB2 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Bstoichiometric TiB₂ | 30 – 31.5 | 31.1 |
| Cresidual from carbothermal synthesis | ≤ 0.5 | 0.2 |
| Osurface oxide on powder | ≤ 1 | 0.4 |
| Femilling pickup | ≤ 0.2 | 0.05 |
| N | ≤ 0.3 | 0.1 |
| Ti≈68.9 wt % nominal | balance | — |
TiB2 HIP — frequently asked
What is TiB2 HIP used for?
TiB2 HIP is typically used for evaporation boats for metallizing, cutting tool inserts, armor tiles and wear-resistant coatings. In short: EDM-machinable ultra-hard ceramic; conductive boride wear material; high modulus at 4.5 g/cm³.
Is TiB2 HIP easy to machine?
Not especially — machinability is rated not recommended (5/100, worse than 59% of ceramic grades). After sintering only diamond grinding and lapping apply, but the low electrical resistivity allows wire and sinker EDM — the main machining advantage of TiB₂ over other ultra-hard ceramics.
Can TiB2 HIP be welded?
Not fusion weldable; join to metals by active brazing with Ti- or Zr-bearing fillers, or by mechanical clamping. Match thermal expansion to avoid cracking.
What surface finishes work on TiB2 HIP?
Diamond lapping and polishing reach Ra < 0.1 µm. No plating or painting; SiC or oxide coatings can be added to suppress oxidation above 900 °C.
Can TiB2 HIP be formed, bent or molded?
Near-net shape comes from cold isostatic pressing of powder plus pressureless sintering, or hot pressing in graphite dies at 1800–2000 °C and 20–30 MPa; HIP is used for fully dense complex parts.
What is the maximum service temperature of TiB2 HIP?
TiB2 HIP is rated for continuous use to about 950°C (1,742 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- Engineered Materials Handbook Vol. 4: Ceramics and Glasses — ASM International (1991)
- Handbook of Refractory Carbides and Nitrides / Boride property tables — Noyes/Elsevier (1996)
- Titanium Diboride (TiB₂) technical ceramic datasheet — CoorsTek (2023)
- Boride ceramics and evaporation boat materials — Kennametal / Momentive-type boat producers (2022)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.