TiB2 vs ZrB2
Ceramic · grade comparison
TiB2 and ZrB2 are both ceramic grades. TiB2 is harder — 3,000 HV against 2,200 HV for ZrB2 — which matters for wear surfaces and threads. TiB2 is lighter (4.5 g/cm³ vs 6.09 g/cm³ for ZrB2) and TiB2 is stiffer (550 GPa vs 489 GPa).
TiB2Choose it when surface hardness matters, or when weight is the constraint.
ZrB2Choose it when the part sees heat.
TiB2 vs ZrB2: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all ceramic grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Compressive Strength
Flexural Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Tensile Strength (Ultimate)
Same in both: Hardness, Mohs 9
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Same in both: Porosity 1%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 70 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Sintering / Firing Temperature
Same in both: Polishability 75 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Thermal Diffusivity
Strength versus weight
Yield strength against density for every ceramic grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | TiB2 | ZrB2 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
TiB2 vs ZrB2 — frequently asked
What is the difference between TiB2 and ZrB2?
TiB2 and ZrB2 are both ceramic grades. TiB2 is harder — 3,000 HV against 2,200 HV for ZrB2 — which matters for wear surfaces and threads. TiB2 is lighter (4.5 g/cm³ vs 6.09 g/cm³ for ZrB2) and TiB2 is stiffer (550 GPa vs 489 GPa).
Which is cheaper, TiB2 or ZrB2?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose TiB2 over ZrB2?
Pick TiB2 when surface hardness matters, or when weight is the constraint. Pick ZrB2 when the part sees heat.