PLZT 9/65/35-HIP
Grade
9/65/35-HIP = pLZT 9/65/35 HIP
Specify the hot isostatically pressed version when maximum transmission, minimum scattering and larger optical window sizes are needed, at 7.92 g/cm³ density and the highest cost.
Values for the 9/65/35-HIP condition
Other PLZT tempers and conditions
PLZT is listed in 4 conditions; see the grade overview at PLZT.
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
9/65/35Default PLZT 9/65/35 | Choose the hot-pressed relaxor composition for optical shutters, modulators and goggles: relaxor at room temperature, no residual birefringence and a large Kerr effect, but limited to 80 °C. | — | 40 | 0.05 | 380 HV | 1 W/m·K |
PLZT 8/65/35 | Choose when a latchable remanent polarization is needed at room temperature — optical and image storage, bistable light shutters — with the ferroelectric phase retained only to 110 °C. | — | 40 | 0.05 | 385 HV | 1 W/m·K |
9/65/35-HIPThis page PLZT 9/65/35 HIP | Specify the hot isostatically pressed version when maximum transmission, minimum scattering and larger optical window sizes are needed, at 7.92 g/cm³ density and the highest cost. | — | 45 | 0.05 | 390 HV | 1 W/m·K |
PLZT 2/95/5 | Pick for field-induced antiferroelectric–ferroelectric switching: low permittivity, high withstand voltage and large volume strain for energy storage, explosive-electric transduction and high-strain actuation to 180 °C. | — | 45 | 0.05 | 400 HV | 2 W/m·K |
What is PLZT 9/65/35-HIP?
PLZT 9/65/35-HIP is PLZT in the 9/65/35-HIP grade — specify the hot isostatically pressed version when maximum transmission, minimum scattering and larger optical window sizes are needed, at 7.92 g/cm³ density and the highest cost. PLZT 9/65/35-HIP has a tensile strength of 45 MPa (6.53 ksi), weaker than 69% of ceramic grades. Elongation at break is 0.05% and the elastic modulus is 70 GPa (10.2 Msi). PLZT 9/65/35-HIP has a density of 7.92 g/cm³ (0.286 lb/in³), heavier than 77% of ceramic grades. It melts at 1,300°C (2,372 °F). 9/65/35 is the default condition FabDigit quotes; 9/65/35-HIP is available on request or by drawing note.
Advantages
- Polishes to a fine finish — 95/100, better than 97% of ceramic grades
Limitations
- Limited service temperature — 80°C (176 °F), worse than 100% of ceramic grades
- Poor heat conductor — 1.4 W/m·K (0.78 BTU/hr·ft·°F), worse than 93% of ceramic grades
- Low stiffness — 70 GPa (10.2 Msi), worse than 79% of ceramic grades
- Heavy — 7.92 g/cm³ (0.286 lb/in³), worse than 77% of ceramic grades
PLZT 9/65/35-HIP properties
Typical room-temperature values for PLZT 9/65/35-HIP; 19 are specific to this condition. Other listed values are PLZT reference data and may not represent this condition. Bars are the position among ceramic grades.
Physical5
PLZT 9/65/35-HIP has a density of 7.92 g/cm³ (0.286 lb/in³), heavier than 77% of ceramic grades. It melts at 1,300°C (2,372 °F).
Mechanical13
PLZT 9/65/35-HIP has a tensile strength of 45 MPa (6.53 ksi), weaker than 69% of ceramic grades. Elongation at break is 0.05% and the elastic modulus is 70 GPa (10.2 Msi).
Thermal5
PLZT 9/65/35-HIP is rated for continuous service to 80°C (176 °F). It conducts heat at 1.4 W/m·K (0.78 BTU/hr·ft·°F), worse than 93% of ceramic grades. Thermal expansion is 5 µm/m·K (2.78 µin/in·°F).
Electrical5
PLZT 9/65/35-HIP is an electrical insulator with a dielectric strength of 13 kV/mm (330.2 V/mil) and a resistivity of 2×10¹⁰ Ω·m.
Chemical & Environmental2
Corrosion resistance is good (62/100), worse than 70% of ceramic grades.
Sustainability4
Producing a kilogram of PLZT 9/65/35-HIP takes about 100 MJ of energy and emits 9 kg of CO₂ — less than 55% of ceramic grades. Typical recycled content is 0%.
Manufacturability3
PLZT 9/65/35-HIP's machinability is not recommended (7/100, better than 63% of ceramic grades).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with PLZT 9/65/35-HIP
Is PLZT easy to machine?
Machine only with diamond wheels or wire saws followed by lapping and polishing; sintered PLZT cannot be turned or milled. Thin plates chip readily, so use low feed rates and water cooling.
Can PLZT be welded?
Not weldable. Assemble to metals or optics with epoxy adhesive, glass solder, or by brazing to a metallised layer (Cr/Ni/Au or electroless Ni).
Can PLZT be formed, bent or molded?
Formed from co-precipitated or mixed-oxide powder by cold isostatic pressing, then densified by hot pressing or hot isostatic pressing in a PbO atmosphere; lead volatilisation and stoichiometry must be closely controlled.
What surface finishes work on PLZT?
Lap and polish both faces to λ/4 flatness and apply AR coatings; electrodes are usually sputtered transparent ITO or evaporated Cr/Au, and poled parts are aged below the Curie temperature to stabilise properties.
PLZT chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| PbA-site host; (Pb0.91La0.09) for 9/65/35 | 55 – 61 | 58.3 |
| Ladopant level = first digit of grade (at% A-site substitution) | 1 – 5 | 3.9 |
| ZrB-site; Zr/Ti = 65/35 | 14 – 25 | 17.9 |
| TiB-site | 1 – 6 | 5.1 |
| Ooxygen site of the perovskite ABO3 lattice | balance | — |
PLZT 9/65/35-HIP — frequently asked
What is PLZT 9/65/35-HIP used for?
PLZT 9/65/35-HIP is typically used for optical shutters, electro-optic modulators, flash-blindness goggles and actuators. In short: transparent electro-optic PZT; optical-grade piezo ceramic; low 80 °C service limit.
What is the tensile strength of PLZT 9/65/35-HIP?
PLZT 9/65/35-HIP has a typical tensile strength of 45 MPa (6.53 ksi) — weaker than 69% of ceramic grades. Strength varies by condition: see the 4 listed tempers.
Is PLZT 9/65/35-HIP easy to machine?
Not especially — machinability is rated not recommended (7/100, better than 63% of ceramic grades). Machine only with diamond wheels or wire saws followed by lapping and polishing; sintered PLZT cannot be turned or milled. Thin plates chip readily, so use low feed rates and water cooling.
Can PLZT 9/65/35-HIP be welded?
Not weldable. Assemble to metals or optics with epoxy adhesive, glass solder, or by brazing to a metallised layer (Cr/Ni/Au or electroless Ni).
What surface finishes work on PLZT 9/65/35-HIP?
Lap and polish both faces to λ/4 flatness and apply AR coatings; electrodes are usually sputtered transparent ITO or evaporated Cr/Au, and poled parts are aged below the Curie temperature to stabilise properties.
Can PLZT 9/65/35-HIP be formed, bent or molded?
Formed from co-precipitated or mixed-oxide powder by cold isostatic pressing, then densified by hot pressing or hot isostatic pressing in a PbO atmosphere; lead volatilisation and stoichiometry must be closely controlled.
What is the maximum service temperature of PLZT 9/65/35-HIP?
PLZT 9/65/35-HIP is rated for continuous use to about 80°C (176 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- Engineered Materials Handbook Vol. 4: Ceramics and Glasses — Electro-optic ceramics — ASM International (1991)
- Haertling, 'Ferroelectric Ceramics: History and Technology', J. Am. Ceram. Soc. 82[4] — American Ceramic Society (1999)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.