Steel P5 Normalized
Heat-treated state
AISI/SAE P5 · UNS T51605
Used after heavy forging or hubbing to refine grain and homogenize structure before the sub-critical anneal.
Values for the Normalized condition
Other P5 tempers and conditions
P5 is listed in 4 conditions; see the grade overview at P5.
- Annealed
- Normalized
- Carburized-HT
- Carburized-HT-Cr
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
AnnealedDefault soft, as-supplied condition for machining and cold hubbing | Standard stock condition: maximum softness (105–116 HB) for cavity hubbing, machining and engraving before carburizing. | 290 | 490 | 30 | 110 HB | — |
NormalizedThis page 900–925 °C air cool, grain refinement before final machining | Used after heavy forging or hubbing to refine grain and homogenize structure before the sub-critical anneal. | 340 | 560 | 26 | 150 HB | 35 W/m·K |
case 58–64 HRC | Final service condition: pack/gas carburize 900–925 °C, quench from ~790–830 °C, temper 175–260 °C for a hard wear-resistant case over a tough low-carbon core. | 750 | 1,000 | 12 | 62 HRC | — |
Carburized, hardened and hard-chrome plated cavity | Choose when molding corrosive resins (PVC, FR grades) or when extra cavity wear life and release are needed. | 760 | 950 | 14 | 66 HRC | 7.5 % IACS |
What is P5 Normalized?
P5 Normalized is P5 heat treated to Normalized — used after heavy forging or hubbing to refine grain and homogenize structure before the sub-critical anneal. P5 Normalized has a yield strength of 340 MPa (49.3 ksi) and a tensile strength of 560 MPa (81.2 ksi) — weaker than 76% of steel grades. Elongation at break is 26% and the elastic modulus is 205 GPa (29.7 Msi). P5 Normalized has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,425°C (2,597 °F). Annealed is the default condition FabDigit quotes; Normalized is available on request or by drawing note.
Advantages
- Easy to machine — 65/100, better than 93% of steel grades
- Polishes to a fine finish — 70/100, better than 87% of steel grades
- Ductile — tolerates forming and impact — 26%, better than 82% of steel grades
- Forms and bends easily — 65/100, better than 81% of steel grades
Limitations
- Limited service temperature — 200°C (392 °F), worse than 93% of steel grades
- Low strength — 340 MPa (49.3 ksi), worse than 76% of steel grades
- Poor heat conductor — 35 W/m·K (20.2 BTU/hr·ft·°F), worse than 75% of steel grades
P5 Normalized properties
Typical room-temperature values for P5 Normalized; 21 are specific to this condition. Other listed values are P5 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
P5 Normalized has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,425°C (2,597 °F).
Mechanical15
P5 Normalized has a yield strength of 340 MPa (49.3 ksi) and a tensile strength of 560 MPa (81.2 ksi) — weaker than 76% of steel grades. Elongation at break is 26% and the elastic modulus is 205 GPa (29.7 Msi).
Thermal6
P5 Normalized is rated for continuous service to 200°C (392 °F). It conducts heat at 35 W/m·K (20.2 BTU/hr·ft·°F), worse than 75% of steel grades. Thermal expansion is 12.4 µm/m·K (6.89 µin/in·°F).
Electrical3
P5 Normalized conducts electricity at 8 % IACS, better than 55% of steel grades.
Chemical & Environmental3
Corrosion resistance is poor (15/100), better than 75% of steel grades.
Sustainability4
Producing a kilogram of P5 Normalized takes about 32 MJ of energy and emits 2.3 kg of CO₂ — more than 70% of steel grades. Typical recycled content is 40%.
Manufacturability5
P5 Normalized's machinability is good (65/100, better than 93% of steel grades); weldability fair (52/100); formability good (65/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with P5 Normalized
Is P5 easy to machine?
Very easy to machine and engrave in the annealed state (~70% of AISI 1212), but the soft low-carbon matrix tends to smear — use sharp positive-rake tools and finish before carburizing; after case hardening only grinding/EDM apply.
Can P5 be welded?
Low carbon makes repair welding practical with matching low-alloy or Ni-based filler; preheat 200–300 °C, and re-carburize or at least re-temper the repaired area.
Can P5 be formed, bent or molded?
Designed for cold hubbing (hobbing) of cavities — the master hub is pressed into the annealed blank, with stress-relief anneals between passes; hot forge 1050–1150 °C, finish above 900 °C.
What surface finishes work on P5?
Carburized case takes a high polish and texture well; hard chrome or electroless nickel plating is common for corrosive resins and added wear life; keep oiled or plated as the alloy rusts freely.
P5 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Clow carbon for carburizing / cold hubbing | ≤ 0.1 | 0.1 |
| Mn | 0.2 – 0.6 | 0.4 |
| Si | 0.1 – 0.4 | 0.25 |
| Crgives the harder, more wear-resistant case vs P2/P3 | 2 – 2.5 | 2.25 |
| Nioptional residual/addition | ≤ 0.35 | 0.2 |
| P | ≤ 0.03 | — |
| S | ≤ 0.03 | — |
| Fe | balance | — |
P5 Normalized — frequently asked
What is P5 Normalized used for?
P5 Normalized is typically used for carburized mold inserts, die components requiring hard cases and small precision molds. In short: easiest P-series to hob; higher-chromium case; best formability in family.
What is the yield strength of P5 Normalized?
P5 Normalized has a typical yield strength of 340 MPa (49.3 ksi) and a tensile strength of 560 MPa (81.2 ksi) — weaker than 76% of steel grades. Strength varies by condition: see the 4 listed tempers.
Is P5 Normalized easy to machine?
Reasonably — machinability is rated good (65/100, better than 93% of steel grades). Very easy to machine and engrave in the annealed state (~70% of AISI 1212), but the soft low-carbon matrix tends to smear — use sharp positive-rake tools and finish before carburizing; after case hardening only grinding/EDM apply.
Can P5 Normalized be welded?
With care — weldability is rated fair (52/100). Low carbon makes repair welding practical with matching low-alloy or Ni-based filler; preheat 200–300 °C, and re-carburize or at least re-temper the repaired area.
What surface finishes work on P5 Normalized?
Carburized case takes a high polish and texture well; hard chrome or electroless nickel plating is common for corrosive resins and added wear life; keep oiled or plated as the alloy rusts freely.
Can P5 Normalized be formed, bent or molded?
Designed for cold hubbing (hobbing) of cavities — the master hub is pressed into the annealed blank, with stress-relief anneals between passes; hot forge 1050–1150 °C, finish above 900 °C.
What is the maximum service temperature of P5 Normalized?
P5 Normalized is rated for continuous use to about 200°C (392 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- ASTM A681 — Standard Specification for Tool Steels Alloy — ASTM International (2022)
- ASM Handbook Vol. 1: Properties and Selection — Irons, Steels, and High-Performance Alloys (Tool Steels: P-type mold steels) — ASM International (1990)
- ASM Handbook Vol. 4: Heat Treating — Heat Treating of Tool Steels — ASM International (1991)
- Tool Steels, 5th Edition (Roberts, Krauss, Kennedy) — ASM International (1998)
- UNS T51605 alloy data — SAE/ASTM Unified Numbering System (2017)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.