Precious Metal Pt950 As Cast
Finish state
Use as-cast investment or centrifugal castings for complex small jewellery parts; coarse grain and some shrinkage porosity hold tensile strength to 350 MPa, below wrought material.
Values for the As Cast condition
Other Pt950 tempers and conditions
Pt950 is listed in 4 conditions; see the grade overview at Pt950.
- O
- As Cast
- Stress Relieved
- Cold Worked
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
ODefault Annealed | Pick the annealed, recrystallized temper as standard stock for sheet, strip, wire and tube: 35 % elongation suits stamping, drawing, stone setting and further cold forming, at the lowest strength. | 130 | 310 | 35 | 105 HB | — |
As CastThis page investment / centrifugal cast, no post heat treatment | Use as-cast investment or centrifugal castings for complex small jewellery parts; coarse grain and some shrinkage porosity hold tensile strength to 350 MPa, below wrought material. | 175 | 350 | 22 | 124 HB | 7 % IACS |
low-temperature stress relief after cold work or welding | Use a low-temperature stress relief after cold work or welding to remove internal stress while keeping part of the cold-work strength, preventing cracked settings or dimensional drift. | 250 | 400 | 20 | 142 HB | 7 % IACS |
hard temper (approx. 40–60 % reduction) | Choose the hard temper from roughly 40–60 % cold reduction for spring wire, prongs, electrode wire and fine tubing needing 560 MPa yield and wear resistance; elongation falls to 3 %. | 560 | 650 | 3 | 235 HB | — |
What is Pt950 As Cast?
Pt950 As Cast is Pt950 supplied in the As Cast condition — use as-cast investment or centrifugal castings for complex small jewellery parts; coarse grain and some shrinkage porosity hold tensile strength to 350 MPa, below wrought material. Pt950 As Cast has a yield strength of 175 MPa (25.4 ksi) and a tensile strength of 350 MPa (50.8 ksi) — weaker than 62% of precious metal grades. Elongation at break is 22% and the elastic modulus is 170 GPa (24.7 Msi). Pt950 As Cast has a density of 20.1 g/cm³ (0.726 lb/in³), heavier than 94% of precious metal grades. It melts at 1,755°C (3,191 °F). O is the default condition FabDigit quotes; As Cast is available on request or by drawing note.
Advantages
- Good corrosion resistance — 100/100, better than 98% of precious metal grades
- High service temperature — 1,200°C (2,192 °F), better than 97% of precious metal grades
- Readily welded — 85/100, better than 93% of precious metal grades
- Stiff — 170 GPa (24.7 Msi), better than 90% of precious metal grades
Limitations
- High embodied carbon — 16,000 kg CO₂/kg, worse than 96% of precious metal grades
- Heavy — 20.1 g/cm³ (0.726 lb/in³), worse than 94% of precious metal grades
- Low electrical conductivity — 7 % IACS, worse than 89% of precious metal grades
- Limited formability — 60/100, worse than 87% of precious metal grades
- Poor heat conductor — 39 W/m·K (22.5 BTU/hr·ft·°F), worse than 86% of precious metal grades
Pt950 As Cast properties
Typical room-temperature values for Pt950 As Cast; 21 are specific to this condition. Other listed values are Pt950 reference data and may not represent this condition. Bars are the position among precious metal grades.
Physical3
Pt950 As Cast has a density of 20.1 g/cm³ (0.726 lb/in³), heavier than 94% of precious metal grades. It melts at 1,755°C (3,191 °F).
Mechanical11
Pt950 As Cast has a yield strength of 175 MPa (25.4 ksi) and a tensile strength of 350 MPa (50.8 ksi) — weaker than 62% of precious metal grades. Elongation at break is 22% and the elastic modulus is 170 GPa (24.7 Msi).
Thermal6
Pt950 As Cast is rated for continuous service to 1,200°C (2,192 °F). It conducts heat at 39 W/m·K (22.5 BTU/hr·ft·°F), worse than 86% of precious metal grades. Thermal expansion is 9 µm/m·K (5 µin/in·°F).
Electrical3
Pt950 As Cast conducts electricity at 7 % IACS, worse than 89% of precious metal grades.
Chemical & Environmental3
Corrosion resistance is excellent (100/100), better than 98% of precious metal grades.
Sustainability4
Producing a kilogram of Pt950 As Cast takes about 250,000 MJ of energy and emits 16,000 kg of CO₂ — more than 95% of precious metal grades. Typical recycled content is 35%.
Manufacturability8
Pt950 As Cast's machinability is poor (32/100, worse than 80% of precious metal grades); weldability excellent (85/100); formability good (60/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Pt950 As Cast
Is Pt950 easy to machine?
Highly prone to sticking and built-up edge: use sharp positive-rake carbide or diamond tools at high speed and low feed with generous lubrication. Recover all chips and grinding dust for refining.
Can Pt950 be welded?
Laser spot welding, pulsed TIG and oxy-hydrogen torch welding all perform well and can be run autogenously without flux. Avoid Pb, Bi, S and Si contamination and contact with silicon-bearing refractories, which cause high-temperature embrittlement.
Can Pt950 be formed, bent or molded?
Cold formability in the annealed temper is excellent, above 90 % deformation, with interstage anneals at 900–1000 °C. Casting requires vacuum or centrifugal equipment, zirconia or yttria shells and a pouring temperature of about 1850–1900 °C.
What surface finishes work on Pt950?
Takes a mirror polish directly and needs no plating; sandblasting, brushing and laser engraving are all practical. Use dust extraction during polishing to recover precious metal fines.
Pt950 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| RuPt950Ru: most common wrought/cast jewellery variant | 0 – 5 | 5 |
| IrPt950Ir (Pt-Ir 950): best ductility; wire, electrodes, medical | 0 – 5 | — |
| CoPt950Co: best casting flow, high as-cast hardness, weakly magnetic | 0 – 5 | — |
| CuPt950Cu: lower cost, medium hardness, common in EU/Asia jewellery | 0 – 5 | — |
| PdPt950Pd: soft, easily worked; used for prongs and solder joints | 0 – 5 | — |
| WPt950W: high-hardness wrought variant | 0 – 5 | — |
| other (total)Fe, Si, Pb, Bi limited; Pb/Bi cause high-temp embrittlement | 0 – 0.15 | — |
| PtPt950 / 950 hallmark requires at least 95.0 wt% platinum | ≥ 95 (balance) | — |
Pt950 As Cast — frequently asked
What is Pt950 As Cast used for?
Pt950 As Cast is typically used for bridal jewelry and wedding bands, watch cases and bezels, laboratory crucibles and dishes, electrodes, thermocouple sheaths and medical implant components. In short: premium platinum jewelry alloy.
What is the yield strength of Pt950 As Cast?
Pt950 As Cast has a typical yield strength of 175 MPa (25.4 ksi) and a tensile strength of 350 MPa (50.8 ksi) — weaker than 62% of precious metal grades. Strength varies by condition: see the 4 listed tempers.
Is Pt950 As Cast easy to machine?
Not especially — machinability is rated poor (32/100, worse than 80% of precious metal grades). Highly prone to sticking and built-up edge: use sharp positive-rake carbide or diamond tools at high speed and low feed with generous lubrication. Recover all chips and grinding dust for refining.
Can Pt950 As Cast be welded?
Yes — weldability is rated excellent (85/100). Laser spot welding, pulsed TIG and oxy-hydrogen torch welding all perform well and can be run autogenously without flux. Avoid Pb, Bi, S and Si contamination and contact with silicon-bearing refractories, which cause high-temperature embrittlement.
What surface finishes work on Pt950 As Cast?
Takes a mirror polish directly and needs no plating; sandblasting, brushing and laser engraving are all practical. Use dust extraction during polishing to recover precious metal fines.
Can Pt950 As Cast be formed, bent or molded?
Cold formability in the annealed temper is excellent, above 90 % deformation, with interstage anneals at 900–1000 °C. Casting requires vacuum or centrifugal equipment, zirconia or yttria shells and a pouring temperature of about 1850–1900 °C.
What is the maximum service temperature of Pt950 As Cast?
Pt950 As Cast is rated for continuous use to about 1,200°C (2,192 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- ASM Handbook Vol.2: Properties and Selection — Nonferrous Alloys (Precious Metals) — ASM International (1990)
- ASM Handbook Vol.13B: Corrosion — Materials (Platinum Group Metals) — ASM International (2005)
- Platinum jewellery alloy data (Pt950Ru / Pt950Ir / Pt950Co) — Johnson Matthey / PGM refiners (2021)
- ASTM B684 / B561 — Platinum and platinum alloy products — ASTM (2019)
- Precious metal LCA / embodied energy datasets — Granta / ecoinvent (2022)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.