AgCl PC
Heat-treated state
PC = polycrystalline hot-pressed / extruded sheet and rod
Choose for cheap thick gaskets, cold-flow seals, ATR blanks and large-area windows where slight scatter is acceptable.
Values for the PC condition
Other AgCl tempers and conditions
AgCl is listed in 3 conditions; see the grade overview at AgCl.
Compare all 3 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
AgCl–AgBr | Choose when transmission must be extended past 20 µm or when drawing flexible CO2/thermal-imaging IR fibres. | — | 25 | 25 | 12 HV | 1 W/m·K |
SCDefault Single-crystal optical grade | Choose for the highest transmission and lowest scatter IR windows, ATR prisms and lenses over 0.4–28 µm. | — | 26 | 20 | 10 HV | 1 W/m·K |
PCThis page Polycrystalline hot-pressed / extruded sheet and rod | Choose for cheap thick gaskets, cold-flow seals, ATR blanks and large-area windows where slight scatter is acceptable. | — | 32 | 15 | 13 HV | 1 W/m·K |
What is AgCl PC?
AgCl PC is AgCl heat treated to PC — choose for cheap thick gaskets, cold-flow seals, ATR blanks and large-area windows where slight scatter is acceptable. AgCl PC has a tensile strength of 32 MPa (4.64 ksi), weaker than 77% of glass grades. Elongation at break is 15% and the elastic modulus is 21 GPa (3.05 Msi). AgCl PC has a density of 5.56 g/cm³ (0.201 lb/in³), heavier than 95% of glass grades. It melts at 455°C (851 °F). SC is the default condition FabDigit quotes; PC is available on request or by drawing note.
Advantages
- Ductile — tolerates forming and impact — 15%, better than 98% of glass grades
- Easy to machine — 35/100, better than 77% of glass grades
Limitations
- Hard to polish — 40/100, worse than 97% of glass grades
- Heavy — 5.56 g/cm³ (0.201 lb/in³), worse than 95% of glass grades
- Low stiffness — 21 GPa (3.05 Msi), worse than 92% of glass grades
- High embodied carbon — 80 kg CO₂/kg, worse than 92% of glass grades
- Limited service temperature — 180°C (356 °F), worse than 90% of glass grades
AgCl PC properties
Typical room-temperature values for AgCl PC; 15 are specific to this condition. Other listed values are AgCl reference data and may not represent this condition. Bars are the position among glass grades.
Physical5
AgCl PC has a density of 5.56 g/cm³ (0.201 lb/in³), heavier than 95% of glass grades. It melts at 455°C (851 °F).
Mechanical13
AgCl PC has a tensile strength of 32 MPa (4.64 ksi), weaker than 77% of glass grades. Elongation at break is 15% and the elastic modulus is 21 GPa (3.05 Msi).
Thermal5
AgCl PC is rated for continuous service to 180°C (356 °F). It conducts heat at 1.1 W/m·K (0.607 BTU/hr·ft·°F), worse than 73% of glass grades. Thermal expansion is 30 µm/m·K (16.7 µin/in·°F).
Electrical3
AgCl PC has an electrical resistivity of 8×10⁸ Ω·m.
Chemical & Environmental2
Corrosion resistance is very good (70/100), worse than 58% of glass grades.
Sustainability4
Producing a kilogram of AgCl PC takes about 1,200 MJ of energy and emits 80 kg of CO₂ — more than 92% of glass grades. Typical recycled content is 40%.
Manufacturability2
AgCl PC's machinability is fair (35/100, better than 77% of glass grades).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with AgCl PC
Is AgCl easy to machine?
Extremely soft and gummy — single-point diamond turning with light cuts, or shear/punch cold; avoid abrasive grinding which smears and embeds silver.
Can AgCl be welded?
Not welded; parts are cold-pressed, extruded or diffusion-bonded silver-halide to silver-halide at 150–250 °C.
Can AgCl be formed, bent or molded?
Fully ductile: can be cold rolled, extruded into sheet, rod and fibre, and coined into gaskets or ATR prism shapes without cracking.
What surface finishes work on AgCl?
Diamond-turn or lightly polish with soft cloth and dilute thiosulfate-free slurry; store in the dark and handle with gloves — light exposure and contact with Al/Cu darkens the surface; AR coatings must be low-temperature deposited.
AgCl chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Agstoichiometric silver | 75 – 75.5 | 75.26 |
| Clstoichiometric chlorine | ≥ 24.5 (balance) | — |
AgCl PC — frequently asked
What is AgCl PC used for?
AgCl PC is typically used for IR windows, IR fiber optics and electrochemical reference electrodes. In short: ductile IR crystal; non-hygroscopic KBr alternative; light-sensitive, store dark.
What is the tensile strength of AgCl PC?
AgCl PC has a typical tensile strength of 32 MPa (4.64 ksi) — weaker than 77% of glass grades. Strength varies by condition: see the 3 listed tempers.
Is AgCl PC easy to machine?
Not especially — machinability is rated fair (35/100, better than 77% of glass grades). Extremely soft and gummy — single-point diamond turning with light cuts, or shear/punch cold; avoid abrasive grinding which smears and embeds silver.
Can AgCl PC be welded?
Not welded; parts are cold-pressed, extruded or diffusion-bonded silver-halide to silver-halide at 150–250 °C.
What surface finishes work on AgCl PC?
Diamond-turn or lightly polish with soft cloth and dilute thiosulfate-free slurry; store in the dark and handle with gloves — light exposure and contact with Al/Cu darkens the surface; AR coatings must be low-temperature deposited.
Can AgCl PC be formed, bent or molded?
Fully ductile: can be cold rolled, extruded into sheet, rod and fibre, and coined into gaskets or ATR prism shapes without cracking.
What is the maximum service temperature of AgCl PC?
AgCl PC is rated for continuous use to about 180°C (356 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- CRC Handbook of Chemistry and Physics — silver chloride physical data — CRC Press (2022)
- Handbook of Optical Constants of Solids — Academic Press (1998)
- Silver Chloride (AgCl) IR optical material data — Crystran Ltd (2023)
- IR crystal materials comparison tables — ISP Optics / LightPath (2022)
- Infrared fibre and silver-halide crystal property data — SPIE / journal literature (2019)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.