Titanium Ti-10-2-3 vs Ti-15Mo
Titanium · grade comparison
Titanium Ti-10-2-3 and Ti-15Mo are both titanium grades. Ti-10-2-3 is the stronger of the two: yield strength 930 MPa (135 ksi) against 570 MPa (82.7 ksi) for Ti-15Mo, about 63% more; tensile strength follows at 1,000 MPa (145 ksi) vs 760 MPa (110 ksi). In exchange, Ti-15Mo is the more ductile: elongation 22% versus 12% for Ti-10-2-3, and Ti-10-2-3 is harder (32 HRC vs 27 HRC). Ti-10-2-3 is lighter (4.65 g/cm³ vs 4.96 g/cm³ for Ti-15Mo) and Ti-10-2-3 is stiffer (110 GPa vs 78 GPa). On the shop floor, Ti-15Mo welds better (very good vs fair) and Ti-15Mo sits in a lower cost tier (high, $$$$) than Ti-10-2-3 (specialty, $$$$$).
Ti-10-2-3Choose it when strength drives the design, or when weight is the constraint.
Ti-15MoChoose it when the part is bent, formed or impact-loaded, or when it will be welded.
Ti-10-2-3 vs Ti-15Mo: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Rockwell C
Hardness, Vickers
Charpy V-Notch Impact (RT)
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Specific Heat Capacity 500 J/kg·K0.12 BTU/lb·°F · Max Service Temperature (continuous) 300°C572 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 1.2 % IACS · Electrical Resistivity 1.4×10⁻⁶ Ω·m55.1 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.1 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 18%
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Shock Resistance Index
Same in both: Thermal Diffusivity 3.4 mm²/s
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Ti-10-2-3 | Ti-15Mo |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 1 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Anodizing Type II | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
They share 1 finish: Plasma Spray.
Ti-10-2-3 vs Ti-15Mo — frequently asked
Is Ti-10-2-3 stronger than Ti-15Mo?
Yes. Ti-10-2-3 has a typical yield strength of 930 MPa (135 ksi) against 570 MPa (82.7 ksi) for Ti-15Mo — about 63% more. Tensile strength is 1,000 MPa (145 ksi) vs 760 MPa (110 ksi).
Which is cheaper, Ti-10-2-3 or Ti-15Mo?
Ti-15Mo is the lower-cost material: it sits in the high tier ($$$$) while Ti-10-2-3 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, Ti-10-2-3 or Ti-15Mo?
Ti-15Mo. Its weldability rates very good (72/100) against fair (40/100) for Ti-10-2-3.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Ti-10-2-3 and Ti-15Mo side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.