Titanium Grade 1 vs Ti Grade 26
Titanium · grade comparison
Titanium Grade 1 and Ti Grade 26 are both titanium grades. Ti Grade 26 is the stronger of the two: yield strength 330 MPa (47.9 ksi) against 220 MPa (31.9 ksi) for Grade 1, about 50% more; tensile strength follows at 430 MPa (62.4 ksi) vs 300 MPa (43.5 ksi). In exchange, Grade 1 is the more ductile: elongation 30% versus 24% for Ti Grade 26, and Ti Grade 26 is harder (160 HB vs 120 HB). Grade 1 conducts heat better (20 W/m·K vs 16.4 W/m·K). On the shop floor, Ti Grade 26 sits in a lower cost tier (high, $$$$) than Grade 1 (specialty, $$$$$).
Grade 1Choose it when the part is bent, formed or impact-loaded.
Ti Grade 26Choose it when strength drives the design, or when cost is the deciding factor.
Grade 1 vs Ti Grade 26: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34 · Fracture Toughness (K_IC) 80 MPa·√m72.8 ksi·√in
Physical
Density and transition temperatures.
Melting Point (Solidus)
Same in both: Density 4.51 g/cm³0.16 lb/in³ · Liquidus Temperature 1,670°C3,038 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Same in both: Specific Heat Capacity 523 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F · Latent Heat of Fusion 295 J/g127 BTU/lb · Max Service Temperature (continuous) 300°C572 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Castability
Same in both: Weldability 90 / 100 · Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Same in both: Embodied Energy (primary production) 650 MJ/kg279,450 BTU/lb · Embodied Water 600 L/kg71.9 gal/lb · Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Grade 1 | Ti Grade 26 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 1 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Anodizing Type II | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
They share 1 finish: Plasma Spray.
Grade 1 vs Ti Grade 26 — frequently asked
Is Ti Grade 26 stronger than Grade 1?
Yes. Ti Grade 26 has a typical yield strength of 330 MPa (47.9 ksi) against 220 MPa (31.9 ksi) for Grade 1 — about 50% more. Tensile strength is 430 MPa (62.4 ksi) vs 300 MPa (43.5 ksi).
Which is cheaper, Grade 1 or Ti Grade 26?
Ti Grade 26 is the lower-cost material: it sits in the high tier ($$$$) while Grade 1 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Grade 1 or Ti Grade 26?
Grade 1, by a small margin. Both rate fair for machinability — 42/100 against 35/100 for Ti Grade 26.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Grade 1 and Ti Grade 26 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.