Titanium Grade 1 vs Ti Grade 1
Titanium · grade comparison
Titanium Grade 1 and Ti Grade 1 are both titanium grades. Both yield at about 220 MPa — strength does not separate them. Grade 1 conducts heat better (20 W/m·K vs 16.4 W/m·K). On the shop floor, Ti Grade 1 sits in a lower cost tier (high, $$$$) than Grade 1 (specialty, $$$$$).
Ti Grade 1Choose it when cost is the deciding factor.
Grade 1 vs Ti Grade 1: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Same in both: Elastic (Young's) Modulus 103 GPa14.9 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34 · Reduction in Area 55% · Compressive Strength 250 MPa36.3 ksi · Hardness, Brinell 120 HB · Hardness, Rockwell B 70 HRB · Hardness, Vickers 125 HV
Physical
Density and transition temperatures.
Melting Point (Solidus)
Same in both: Density 4.51 g/cm³0.16 lb/in³ · Liquidus Temperature 1,670°C3,038 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Latent Heat of Fusion
Same in both: Specific Heat Capacity 523 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F · Max Service Temperature (continuous) 300°C572 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Machinability 42 / 100 · Castability 35 / 100 · Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 650 MJ/kg279,450 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 22.8 MN·m/kg
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Grade 1 | Ti Grade 1 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 1 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Anodizing Type II | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
They share 1 finish: Plasma Spray.
Grade 1 vs Ti Grade 1 — frequently asked
What is the difference between Grade 1 and Ti Grade 1?
Titanium Grade 1 and Ti Grade 1 are both titanium grades. Both yield at about 220 MPa — strength does not separate them. Grade 1 conducts heat better (20 W/m·K vs 16.4 W/m·K).
Which is cheaper, Grade 1 or Ti Grade 1?
Ti Grade 1 is the lower-cost material: it sits in the high tier ($$$$) while Grade 1 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
When should I choose Grade 1 over Ti Grade 1?
Pick Ti Grade 1 when cost is the deciding factor.