Titanium C-1 vs Grade Ti-Pd7B
Titanium · grade comparison
Titanium C-1 and Grade Ti-Pd7B are both titanium grades. Grade Ti-Pd7B is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 210 MPa (30.5 ksi) for C-1, about 81% more; tensile strength follows at 450 MPa (65.3 ksi) vs 300 MPa (43.5 ksi). In exchange, C-1 is the more ductile: elongation 20% versus 18% for Grade Ti-Pd7B, and Grade Ti-Pd7B is harder (150 HB vs 120 HB). Grade Ti-Pd7B runs hotter in service (400°C vs 300°C continuous). On the shop floor, C-1 machines more easily (fair vs poor).
C-1Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
Grade Ti-Pd7BChoose it when strength drives the design, or when the part sees heat.
C-1 vs Grade Ti-Pd7B: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 103 GPa14.9 Msi · Poisson's Ratio 0.34 · Reduction in Area 30%
Physical
Density and transition temperatures.
Same in both: Density 4.51 g/cm³0.16 lb/in³ · Melting Point (Solidus) 1,660°C3,020 °F · Liquidus Temperature 1,670°C3,038 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 523 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Same in both: Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 22.8 MN·m/kg
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C-1 | Grade Ti-Pd7B |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 1 finish: Plasma Spray.
C-1 vs Grade Ti-Pd7B — frequently asked
Is Grade Ti-Pd7B stronger than C-1?
Yes. Grade Ti-Pd7B has a typical yield strength of 380 MPa (55.1 ksi) against 210 MPa (30.5 ksi) for C-1 — about 81% more. Tensile strength is 450 MPa (65.3 ksi) vs 300 MPa (43.5 ksi).
Which is cheaper, C-1 or Grade Ti-Pd7B?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, C-1 or Grade Ti-Pd7B?
C-1. Its machinability rates fair (42/100) against poor (32/100) for Grade Ti-Pd7B.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C-1 and Grade Ti-Pd7B side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.