Steel MS1700 vs TRIP1000
Steel · grade comparison
Steel MS1700 and TRIP1000 are both steel grades. MS1700 is the stronger of the two: yield strength 1,450 MPa (210 ksi) against 720 MPa (104 ksi) for TRIP1000, about 101% more; tensile strength follows at 1,780 MPa (258 ksi) vs 1,040 MPa (151 ksi). In exchange, TRIP1000 is the more ductile: elongation 14% versus 4% for MS1700, and MS1700 is harder (50 HRC vs 32 HRC). MS1700 conducts heat better (32 W/m·K vs 28 W/m·K). On the shop floor, TRIP1000 sits in a lower cost tier (budget, $) than MS1700 (standard, $$).
MS1700Choose it when strength drives the design.
TRIP1000Choose it when the part is bent, formed or impact-loaded, or when cost is the deciding factor.
MS1700 vs TRIP1000: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Rockwell C
Hardness, Vickers
Reduction in Area
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Max Service Temperature (continuous) 200°C392 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 45 L/kg5.4 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | MS1700 | TRIP1000 |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | CR | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Black Oxide | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| E-Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
| Tin Plating | Yes | — |
| Zinc Plating | Yes | — |
| Zinc-Flake (Dip-Spin) Coating | Yes | — |
| Zinc-Nickel Plating | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
MS1700 vs TRIP1000 — frequently asked
Is MS1700 stronger than TRIP1000?
Yes. MS1700 has a typical yield strength of 1,450 MPa (210 ksi) against 720 MPa (104 ksi) for TRIP1000 — about 101% more. Tensile strength is 1,780 MPa (258 ksi) vs 1,040 MPa (151 ksi).
Which is cheaper, MS1700 or TRIP1000?
TRIP1000 is the lower-cost material: it sits in the budget tier ($) while MS1700 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, MS1700 or TRIP1000?
TRIP1000, by a small margin. Both rate poor for machinability — 25/100 against 20/100 for MS1700.
Ready to make it?
Upload a CAD file and FabDigit prices the part in MS1700 and TRIP1000 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.