Steel HC300LA vs SPHD
Steel · grade comparison
Steel HC300LA and SPHD are both steel grades. HC300LA is the stronger of the two: yield strength 335 MPa (48.6 ksi) against 230 MPa (33.4 ksi) for SPHD, about 46% more; tensile strength follows at 420 MPa (60.9 ksi) vs 320 MPa (46.4 ksi). In exchange, SPHD is the more ductile: elongation 37% versus 28% for HC300LA, and HC300LA is harder (130 HB vs 100 HB). SPHD runs hotter in service (350°C vs 300°C continuous).
HC300LAChoose it when strength drives the design.
SPHDChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
HC300LA vs SPHD: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Reduction in Area
Compressive Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,495°C2,723 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Machinability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | HC300LA | SPHD |
|---|---|---|
| Sheet metal | — | Yes |
| Default condition | — | HR |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Black Oxide | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| E-Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
| Powder Coating | — | Yes |
| Tin Plating | — | Yes |
| Zinc Plating | — | Yes |
| Zinc-Flake (Dip-Spin) Coating | — | Yes |
| Zinc-Nickel Plating | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
HC300LA vs SPHD — frequently asked
Is HC300LA stronger than SPHD?
Yes. HC300LA has a typical yield strength of 335 MPa (48.6 ksi) against 230 MPa (33.4 ksi) for SPHD — about 46% more. Tensile strength is 420 MPa (60.9 ksi) vs 320 MPa (46.4 ksi).
Which is cheaper, HC300LA or SPHD?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose HC300LA over SPHD?
Pick HC300LA when strength drives the design. Pick SPHD when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in HC300LA and SPHD side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.