Steel A182 F24 vs AR500
Steel · grade comparison
Steel A182 F24 and AR500 are both steel grades. AR500 is the stronger of the two: yield strength 1,350 MPa (196 ksi) against 470 MPa (68.2 ksi) for A182 F24, about 187% more; tensile strength follows at 1,650 MPa (239 ksi) vs 620 MPa (89.9 ksi). In exchange, A182 F24 is the more ductile: elongation 22% versus 9% for AR500, and AR500 is harder (500 HB vs 200 HB). A182 F24 runs hotter in service (570°C vs 250°C continuous) and AR500 conducts heat better (40 W/m·K vs 36 W/m·K). On the shop floor, A182 F24 machines more easily (fair vs not recommended), A182 F24 welds better (good vs fair), and A182 F24 sits in a lower cost tier (premium, $$$) than AR500 (high, $$$$).
A182 F24Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
AR500Choose it when strength drives the design.
A182 F24 vs AR500: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Hardness, Rockwell C
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | A182 F24 | AR500 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | Q&T |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
A182 F24 vs AR500 — frequently asked
Is AR500 stronger than A182 F24?
Yes. AR500 has a typical yield strength of 1,350 MPa (196 ksi) against 470 MPa (68.2 ksi) for A182 F24 — about 187% more. Tensile strength is 1,650 MPa (239 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, A182 F24 or AR500?
A182 F24 is the lower-cost material: it sits in the premium tier ($$$) while AR500 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, A182 F24 or AR500?
A182 F24. Its machinability rates fair (50/100) against not recommended (12/100) for AR500; for welding the order is A182 F24 first (good, 55/100) then AR500 (fair, 45/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in A182 F24 and AR500 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.