Steel 1065 vs 61SiCrV6
Steel · grade comparison
Steel 1065 and 61SiCrV6 are both steel grades. 61SiCrV6 is the stronger of the two: yield strength 1,620 MPa (235 ksi) against 380 MPa (55.1 ksi) for 1065, about 4.3 times as much; tensile strength follows at 1,800 MPa (261 ksi) vs 670 MPa (97.2 ksi). In exchange, 1065 is the more ductile: elongation 12% versus 7% for 61SiCrV6, and 61SiCrV6 is harder (475 HB vs 190 HB). 1065 runs hotter in service (350°C vs 250°C continuous) and 1065 conducts heat better (49 W/m·K vs 33 W/m·K). On the shop floor, 1065 machines more easily (fair vs not recommended), 1065 welds better (poor vs not recommended), and 61SiCrV6 sits in a lower cost tier (budget, $) than 1065 (standard, $$).
1065Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
61SiCrV6Choose it when strength drives the design, or when cost is the deciding factor.
1065 vs 61SiCrV6: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 30%
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Same in both: Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1065 | 61SiCrV6 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | HR | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| HVOF Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
1065 vs 61SiCrV6 — frequently asked
Is 61SiCrV6 stronger than 1065?
Yes. 61SiCrV6 has a typical yield strength of 1,620 MPa (235 ksi) against 380 MPa (55.1 ksi) for 1065 — about 4.3 times as much. Tensile strength is 1,800 MPa (261 ksi) vs 670 MPa (97.2 ksi).
Which is cheaper, 1065 or 61SiCrV6?
61SiCrV6 is the lower-cost material: it sits in the budget tier ($) while 1065 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 1065 or 61SiCrV6?
1065. Its machinability rates fair (45/100) against not recommended (12/100) for 61SiCrV6; for welding the order is 1065 first (poor, 25/100) then 61SiCrV6 (not recommended, 12/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1065 and 61SiCrV6 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.