Steel 100Cr6 and M50NiL are both steel grades. M50NiL is the stronger of the two: yield strength 1,250 MPa (181 ksi) against 420 MPa (60.9 ksi) for 100Cr6, about 198% more; tensile strength follows at 1,500 MPa (218 ksi) vs 660 MPa (95.7 ksi). In exchange, 100Cr6 is the more ductile: elongation 22% versus 12% for M50NiL, and M50NiL is harder (740 HV vs 210 HV). M50NiL runs hotter in service (315°C vs 200°C continuous) and 100Cr6 conducts heat better (45 W/m·K vs 23 W/m·K). On the shop floor, 100Cr6 machines more easily (fair vs not recommended) and 100Cr6 sits in a lower cost tier (standard, $$) than M50NiL (high, $$$$).
100Cr6Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
M50NiLChoose it when strength drives the design, or when the part sees heat.
100Cr6 vs M50NiL: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Fracture Toughness (K_IC)
Hardness, Rockwell C
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 250 J/g107 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Same in both: Weldability 12 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 100Cr6 | M50NiL |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | Annealed | — |
| Relative cost | $$ Standard | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| HVOF Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
100Cr6 vs M50NiL — frequently asked
Is M50NiL stronger than 100Cr6?
Yes. M50NiL has a typical yield strength of 1,250 MPa (181 ksi) against 420 MPa (60.9 ksi) for 100Cr6 — about 198% more. Tensile strength is 1,500 MPa (218 ksi) vs 660 MPa (95.7 ksi).
Which is cheaper, 100Cr6 or M50NiL?
100Cr6 is the lower-cost material: it sits in the standard tier ($$) while M50NiL is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 100Cr6 or M50NiL?
100Cr6. Its machinability rates fair (45/100) against not recommended (8/100) for M50NiL.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 100Cr6 and M50NiL side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.