Stainless Steel 416 vs 420C
Stainless Steel · grade comparison
Stainless Steel 416 and 420C are both stainless steel grades. 420C is the stronger of the two: yield strength 460 MPa (66.7 ksi) against 275 MPa (39.9 ksi) for 416, about 67% more; tensile strength follows at 760 MPa (110 ksi) vs 515 MPa (74.7 ksi). In exchange, 416 is the more ductile: elongation 30% versus 17% for 420C, and 420C is harder (220 HB vs 155 HB). 420C is stiffer (215 GPa vs 200 GPa) and 416 runs hotter in service (650°C vs 400°C continuous). On the shop floor, 416 machines more easily (very good vs fair).
416Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
420CChoose it when strength drives the design.
416 vs 420C: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all stainless steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Compressive Strength
Fracture Toughness (K_IC)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.28
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.7 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Latent Heat of Fusion 260 J/g112 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.35 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Polishability
Castability
Same in both: Formability (cold) 30 / 100 · Brazeability / Solderability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every stainless steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 416 | 420C |
|---|---|---|
| Default condition | Annealed | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining. Both take the same 32 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, CrN, DLC, Electroless Nickel (EN), Electropolishing and 20 more.
416 vs 420C — frequently asked
Is 420C stronger than 416?
Yes. 420C has a typical yield strength of 460 MPa (66.7 ksi) against 275 MPa (39.9 ksi) for 416 — about 67% more. Tensile strength is 760 MPa (110 ksi) vs 515 MPa (74.7 ksi).
Which is cheaper, 416 or 420C?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 416 or 420C?
416. Its machinability rates very good (80/100) against fair (45/100) for 420C.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 416 and 420C side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.