Solder & Low-Melting Alloy Pb65Sn35 vs Pb98Ag2
Solder & Low-Melting Alloy · grade comparison
Solder & Low-Melting Alloy Pb65Sn35 and Pb98Ag2 are both solder & low-melting alloy grades. Pb65Sn35 is the stronger of the two: yield strength 21 MPa (3.05 ksi) against 14 MPa (2.03 ksi) for Pb98Ag2, about 50% more; tensile strength follows at 33 MPa (4.79 ksi) vs 26 MPa (3.77 ksi). Pb65Sn35 is the more ductile: elongation 55% versus 35% for Pb98Ag2, and Pb65Sn35 is harder (12 HB vs 8 HB). Pb65Sn35 is lighter (9.5 g/cm³ vs 11.28 g/cm³ for Pb98Ag2) and Pb65Sn35 is stiffer (26 GPa vs 16.5 GPa).
Pb65Sn35Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Pb98Ag2Choose it when the part sees heat.
Pb65Sn35 vs Pb98Ag2: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 45 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Same in both: Machinability 30 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 300 L/kg35.9 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 2
Strength versus weight
Yield strength against density for every solder & low-melting alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Pb65Sn35 | Pb98Ag2 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Pb65Sn35 vs Pb98Ag2 — frequently asked
Is Pb65Sn35 stronger than Pb98Ag2?
Yes. Pb65Sn35 has a typical yield strength of 21 MPa (3.05 ksi) against 14 MPa (2.03 ksi) for Pb98Ag2 — about 50% more. Tensile strength is 33 MPa (4.79 ksi) vs 26 MPa (3.77 ksi).
Which is cheaper, Pb65Sn35 or Pb98Ag2?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose Pb65Sn35 over Pb98Ag2?
Pick Pb65Sn35 when strength drives the design, or when the part is bent, formed or impact-loaded. Pick Pb98Ag2 when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Pb65Sn35 and Pb98Ag2 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.