Solder & Low-Melting Alloy Pb50Sn50E vs Pb65Sn35
Solder & Low-Melting Alloy · grade comparison
Solder & Low-Melting Alloy Pb50Sn50E and Pb65Sn35 are both solder & low-melting alloy grades. Pb50Sn50E is the stronger of the two: yield strength 27 MPa (3.92 ksi) against 21 MPa (3.05 ksi) for Pb65Sn35, about 29% more; tensile strength follows at 42 MPa (6.09 ksi) vs 33 MPa (4.79 ksi). Pb50Sn50E is harder — 14 HB against 12 HB for Pb65Sn35 — which matters for wear surfaces and threads. Pb50Sn50E is lighter (8.87 g/cm³ vs 9.5 g/cm³ for Pb65Sn35) and Pb50Sn50E conducts heat better (50 W/m·K vs 44 W/m·K).
Pb50Sn50EChoose it when strength drives the design, or when surface hardness matters.
Pb50Sn50E vs Pb65Sn35: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all solder & low-melting alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Shear Modulus 9.5 GPa1.4 Msi · Poisson's Ratio 0.4
Physical
Density and transition temperatures.
Density
Liquidus Temperature
Same in both: Melting Point (Solidus) 183°C361 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Max Service Temperature (continuous) 100°C212 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 45 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Weldability
Same in both: Machinability 30 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every solder & low-melting alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Pb50Sn50E | Pb65Sn35 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Pb50Sn50E vs Pb65Sn35 — frequently asked
Is Pb50Sn50E stronger than Pb65Sn35?
Yes. Pb50Sn50E has a typical yield strength of 27 MPa (3.92 ksi) against 21 MPa (3.05 ksi) for Pb65Sn35 — about 29% more. Tensile strength is 42 MPa (6.09 ksi) vs 33 MPa (4.79 ksi).
Which is cheaper, Pb50Sn50E or Pb65Sn35?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose Pb50Sn50E over Pb65Sn35?
Pick Pb50Sn50E when strength drives the design, or when surface hardness matters.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Pb50Sn50E and Pb65Sn35 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.