Precious Metal BVAu-3 vs BVAu-7
Precious Metal · grade comparison
Precious Metal BVAu-3 and BVAu-7 are both precious metal grades. Both yield at about 210 MPa — strength does not separate them. BVAu-3 is harder — 125 HV against 110 HV for BVAu-7 — which matters for wear surfaces and threads. BVAu-3 is lighter (11.1 g/cm³ vs 12.2 g/cm³ for BVAu-7) and BVAu-3 is stiffer (105 GPa vs 95 GPa). On the shop floor, BVAu-7 forms better (80 vs 70 out of 100).
BVAu-3Choose it when surface hardness matters, or when weight is the constraint.
BVAu-3 vs BVAu-7: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all precious metal grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Shear Strength
Hardness, Vickers
Bulk Modulus
Same in both: Poisson's Ratio 0.35 · Elongation at Break 25%
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -269°C-452 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) 0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Same in both: Machinability 35 / 100 · Weldability 30 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Embodied Water
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every precious metal grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | BVAu-3 | BVAu-7 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
BVAu-3 vs BVAu-7 — frequently asked
What is the difference between BVAu-3 and BVAu-7?
Precious Metal BVAu-3 and BVAu-7 are both precious metal grades. Both yield at about 210 MPa — strength does not separate them. BVAu-3 is harder — 125 HV against 110 HV for BVAu-7 — which matters for wear surfaces and threads.
Which is cheaper, BVAu-3 or BVAu-7?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose BVAu-3 over BVAu-7?
Pick BVAu-3 when surface hardness matters, or when weight is the constraint.
Ready to make it?
Upload a CAD file and FabDigit prices the part in BVAu-3 and BVAu-7 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.