PA610 vs PA66
Polymer · grade comparison
PA610 and PA66 are both polymer grades. PA66 is the stronger of the two: yield strength 80 MPa (11.6 ksi) against 58 MPa (8.41 ksi) for PA610, about 38% more; tensile strength follows at 82 MPa (11.9 ksi) vs 60 MPa (8.7 ksi). In exchange, PA610 is the more ductile: elongation 120% versus 40% for PA66. PA610 is lighter (1.08 g/cm³ vs 1.14 g/cm³ for PA66) and PA66 is stiffer (3 GPa vs 2.2 GPa). On the shop floor, PA66 sits in a lower cost tier (standard, $$) than PA610 (premium, $$$).
PA610Choose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
PA66Choose it when strength drives the design, or when cost is the deciding factor.
PA610 vs PA66: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell M
Hardness, Rockwell R
Fracture Toughness (K_IC)
Physical
Density and transition temperatures.
Density
Melting Temperature (Tm)
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Same in both: Refractive Index 1.53
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Max Service Temperature (short-term)
Same in both: Min Service Temperature -40°C-40 °F · Vicat Softening Point (B50) 200°C392 °F · Limiting Oxygen Index 25%
Electrical
Conductivity and insulation.
Electrical Resistivity
Dissipation Factor (1 MHz)
Volume Resistivity
Same in both: Dielectric Strength 22 kV/mm559 V/mil · Dielectric Constant (1 MHz) 3.4 · Surface Resistivity 1×10¹³ Ω · Comparative Tracking Index (CTI) 600 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Formability (cold)
Polishability
Mold Shrinkage
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Melt Flow Rate
Same in both: Weldability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Same in both: Thermal Diffusivity 0.1 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | PA610 | PA66 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Injection molding | — | Yes |
| Default condition | — | Unfilled |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | — | 0.5 mm |
| Best machined surface | — | Ra 0.8 µm |
| Chrome Plating (Plastic) | — | Yes |
| EMI Shielding Coating | — | Yes |
| Painting | — | Yes |
| Soft Touch Coating | — | Yes |
| Spray Painting | — | Yes |
| UV Coating | — | Yes |
PA610 vs PA66 — frequently asked
Is PA66 stronger than PA610?
Yes. PA66 has a typical yield strength of 80 MPa (11.6 ksi) against 58 MPa (8.41 ksi) for PA610 — about 38% more. Tensile strength is 82 MPa (11.9 ksi) vs 60 MPa (8.7 ksi).
Which is cheaper, PA610 or PA66?
PA66 is the lower-cost material: it sits in the standard tier ($$) while PA610 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, PA610 or PA66?
PA610. Its machinability rates very good (72/100) against good (65/100) for PA66.
Ready to make it?
Upload a CAD file and FabDigit prices the part in PA610 and PA66 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.