FFKM vs HDPE
Polymer · grade comparison
FFKM and HDPE are both polymer grades, both corrosion resistant plastic. HDPE is the stronger of the two: tensile strength 28 MPa (4.06 ksi) against 17 MPa (2.47 ksi) for FFKM, about 65% more. HDPE is the more ductile: elongation 600% versus 140% for FFKM. HDPE is lighter (0.96 g/cm³ vs 2 g/cm³ for FFKM) and HDPE is stiffer (1.1 GPa vs 0.01 GPa). On the shop floor, HDPE machines more easily (very good vs poor) and HDPE sits in a lower cost tier (budget, $) than FFKM (standard, $$).
FFKMChoose it when the part sees heat.
HDPEChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
FFKM vs HDPE: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Shear Strength
Hardness, Shore A
Tear Strength
Compression Set (22 h, 70 °C)
Shear Modulus
Bulk Modulus
Yield Strength (0.2% offset)
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell R
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Melting Temperature (Tm)
Water Absorption (Saturation)
Refractive Index
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Limiting Oxygen Index
Max Service Temperature (short-term)
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Volume Resistivity
Dissipation Factor (1 MHz)
Surface Resistivity
Comparative Tracking Index (CTI)
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Mold Shrinkage
Mold Temperature (typ.)
Weldability
Formability (cold)
Polishability
Melt Flow Rate
Processing Melt Temperature (typ.)
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Embodied Water
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | FFKM | HDPE |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | Semiconductor Grade | FDA Compliant |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | — | 0.5 mm |
| Best machined surface | — | Ra 0.8 µm |
| Painting | — | Yes |
Both are offered for Injection molding. They share 5 finishes: Chrome Plating (Plastic), EMI Shielding Coating, Soft Touch Coating, Spray Painting, UV Coating.
FFKM vs HDPE — frequently asked
Is HDPE stronger than FFKM?
Yes. HDPE has a typical tensile strength of 28 MPa (4.06 ksi) against 17 MPa (2.47 ksi) for FFKM — about 65% more.
Which is cheaper, FFKM or HDPE?
HDPE is the lower-cost material: it sits in the budget tier ($) while FFKM is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, FFKM or HDPE?
HDPE. Its machinability rates very good (75/100) against poor (20/100) for FFKM.
Ready to make it?
Upload a CAD file and FabDigit prices the part in FFKM and HDPE side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.