Nickel 200 vs Nickel 270
Nickel Alloy · grade comparison
Nickel 200 and Nickel 270 are both nickel alloy grades. Nickel 200 is the stronger of the two: yield strength 148 MPa (21.5 ksi) against 105 MPa (15.2 ksi) for Nickel 270, about 41% more; tensile strength follows at 462 MPa (67 ksi) vs 345 MPa (50 ksi). Nickel 200 is harder — 109 HB against 45 HB for Nickel 270 — which matters for wear surfaces and threads. Nickel 270 runs hotter in service (600°C vs 315°C continuous) and Nickel 270 conducts heat better (85 W/m·K vs 70.2 W/m·K). On the shop floor, Nickel 200 machines more easily (fair vs poor) and Nickel 200 sits in a lower cost tier (premium, $$$) than Nickel 270 (high, $$$$).
Nickel 200Choose it when strength drives the design, or when surface hardness matters.
Nickel 270Choose it when the part sees heat.
Nickel 200 vs Nickel 270: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Bulk Modulus 180 GPa26.1 Msi · Poisson's Ratio 0.31 · Charpy V-Notch Impact (RT) 200 J148 ft·lbf
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 8.89 g/cm³0.32 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 456 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 13.3 µm/m·K7.4 µin/in·°F · Latent Heat of Fusion 297 J/g128 BTU/lb · Min Service Temperature -250°C-418 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Same in both: Weldability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Nickel 200 | Nickel 270 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 1.5 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
They share 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
Nickel 200 vs Nickel 270 — frequently asked
Is Nickel 200 stronger than Nickel 270?
Yes. Nickel 200 has a typical yield strength of 148 MPa (21.5 ksi) against 105 MPa (15.2 ksi) for Nickel 270 — about 41% more. Tensile strength is 462 MPa (67 ksi) vs 345 MPa (50 ksi).
Which is cheaper, Nickel 200 or Nickel 270?
Nickel 200 is the lower-cost material: it sits in the premium tier ($$$) while Nickel 270 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Nickel 200 or Nickel 270?
Nickel 200. Its machinability rates fair (35/100) against poor (20/100) for Nickel 270.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Nickel 200 and Nickel 270 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.