Nickel Alloy Hastelloy X vs N06975
Nickel Alloy · grade comparison
Nickel Alloy Hastelloy X and N06975 are both nickel alloy grades. Hastelloy X is the stronger of the two: yield strength 360 MPa (52.2 ksi) against 310 MPa (45 ksi) for N06975, about 16% more; tensile strength follows at 755 MPa (110 ksi) vs 690 MPa (100 ksi). In exchange, N06975 is the more ductile: elongation 50% versus 43% for Hastelloy X, and Hastelloy X is harder (195 HB vs 185 HB). Hastelloy X runs hotter in service (1,150°C vs 540°C continuous) and N06975 conducts heat better (10.5 W/m·K vs 9.1 W/m·K). On the shop floor, Hastelloy X sits in a lower cost tier (premium, $$$) than N06975 (high, $$$$).
Hastelloy XChoose it when strength drives the design, or when the part sees heat.
N06975Choose it when the part is bent, formed or impact-loaded.
Hastelloy X vs N06975: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Fatigue Strength (Endurance Limit) 300 MPa43.5 ksi · Hardness, Rockwell B 90 HRB
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 1.5 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Weldability
Castability
Brazeability / Solderability
Polishability
Same in both: Machinability 18 / 100 · Machinability Rating (AISI 1212 = 100 %) 12% · Formability (cold) 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 35%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Hastelloy X | N06975 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| 3D printing | Yes | — |
| Default condition | Solution Annealed | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 1.5 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
They share 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
Hastelloy X vs N06975 — frequently asked
Is Hastelloy X stronger than N06975?
Yes. Hastelloy X has a typical yield strength of 360 MPa (52.2 ksi) against 310 MPa (45 ksi) for N06975 — about 16% more. Tensile strength is 755 MPa (110 ksi) vs 690 MPa (100 ksi).
Which is cheaper, Hastelloy X or N06975?
Hastelloy X is the lower-cost material: it sits in the premium tier ($$$) while N06975 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, Hastelloy X or N06975?
Hastelloy X. Its weldability rates excellent (85/100) against very good (80/100) for N06975.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Hastelloy X and N06975 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.