Nickel Alloy Hastelloy C276 vs N06255
Nickel Alloy · grade comparison
Nickel Alloy Hastelloy C276 and N06255 are both nickel alloy grades. Both yield at about 360 MPa — strength does not separate them. N06255 is lighter (8.6 g/cm³ vs 8.89 g/cm³ for Hastelloy C276). On the shop floor, Hastelloy C276 sits in a lower cost tier (premium, $$$) than N06255 (high, $$$$).
Hastelloy C276Choose it when cost is the deciding factor.
N06255Choose it when weight is the constraint.
Hastelloy C276 vs N06255: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 79 GPa11.5 Msi · Poisson's Ratio 0.31 · Shear Strength 480 MPa69.6 ksi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Latent Heat of Fusion 290 J/g125 BTU/lb · Max Service Temperature (continuous) 650°C1,202 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.05 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Brazeability / Solderability
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 12% · Weldability 85 / 100 · Formability (cold) 75 / 100 · Castability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 40%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Shock Resistance Index
Same in both: Thermal Diffusivity 2.7 mm²/s
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Hastelloy C276 | N06255 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | Solution Annealed | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 1.5 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
They share 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
Hastelloy C276 vs N06255 — frequently asked
What is the difference between Hastelloy C276 and N06255?
Nickel Alloy Hastelloy C276 and N06255 are both nickel alloy grades. Both yield at about 360 MPa — strength does not separate them. N06255 is lighter (8.6 g/cm³ vs 8.89 g/cm³ for Hastelloy C276).
Which is cheaper, Hastelloy C276 or N06255?
Hastelloy C276 is the lower-cost material: it sits in the premium tier ($$$) while N06255 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
When should I choose Hastelloy C276 over N06255?
Pick Hastelloy C276 when cost is the deciding factor. Pick N06255 when weight is the constraint.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Hastelloy C276 and N06255 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.