Nickel Alloy CW-12MW vs M30H
Nickel Alloy · grade comparison
Nickel Alloy CW-12MW and M30H are both nickel alloy grades. M30H is the stronger of the two: yield strength 520 MPa (75.4 ksi) against 350 MPa (50.8 ksi) for CW-12MW, about 49% more; tensile strength follows at 740 MPa (107 ksi) vs 550 MPa (79.8 ksi). M30H is the more ductile: elongation 15% versus 10% for CW-12MW, and M30H is harder (290 HB vs 200 HB). M30H is lighter (8.3 g/cm³ vs 8.94 g/cm³ for CW-12MW) and CW-12MW is stiffer (205 GPa vs 172 GPa). On the shop floor, CW-12MW welds better (good vs poor).
CW-12MWChoose it when the part sees heat, or when it will be welded.
M30HChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
CW-12MW vs M30H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Machinability Rating (AISI 1212 = 100 %) 12% · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 40%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | CW-12MW | M30H |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
CW-12MW vs M30H — frequently asked
Is M30H stronger than CW-12MW?
Yes. M30H has a typical yield strength of 520 MPa (75.4 ksi) against 350 MPa (50.8 ksi) for CW-12MW — about 49% more. Tensile strength is 740 MPa (107 ksi) vs 550 MPa (79.8 ksi).
Which is cheaper, CW-12MW or M30H?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which welds better, CW-12MW or M30H?
CW-12MW. Its weldability rates good (55/100) against poor (25/100) for M30H.