OSB vs Plywood
Natural Material · grade comparison
OSB and Plywood are both natural material grades. Plywood is the stronger of the two: tensile strength 30 MPa (4.35 ksi) against 12 MPa (1.74 ksi) for OSB, about 150% more. Plywood is lighter (0.55 g/cm³ vs 0.64 g/cm³ for OSB) and Plywood is stiffer (9 GPa vs 3.5 GPa).
PlywoodChoose it when strength drives the design, or when weight is the constraint.
OSB vs Plywood: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all natural material grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all natural material grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Same in both: Elongation at Break 1%
Physical
Density and transition temperatures.
Density
Porosity
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 5%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Same in both: Thermal Diffusivity 0.1 mm²/s · Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every natural material grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | OSB | Plywood |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
OSB vs Plywood — frequently asked
Is Plywood stronger than OSB?
Yes. Plywood has a typical tensile strength of 30 MPa (4.35 ksi) against 12 MPa (1.74 ksi) for OSB — about 150% more.
Which is cheaper, OSB or Plywood?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose OSB over Plywood?
Pick Plywood when strength drives the design, or when weight is the constraint.
Ready to make it?
Upload a CAD file and FabDigit prices the part in OSB and Plywood side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.