Borofloat 33 vs JGS1
Glass · grade comparison
Borofloat 33 and JGS1 are both glass grades. JGS1 is the stronger of the two: tensile strength 50 MPa (7.25 ksi) against 35 MPa (5.08 ksi) for Borofloat 33, about 43% more. JGS1 is harder — 750 HV against 480 HV for Borofloat 33 — which matters for wear surfaces and threads. JGS1 is stiffer (72 GPa vs 64 GPa) and JGS1 runs hotter in service (1,050°C vs 450°C continuous). On the shop floor, Borofloat 33 sits in a lower cost tier (standard, $$) than JGS1 (high, $$$$).
Borofloat 33Choose it when cost is the deciding factor.
JGS1Choose it when strength drives the design, or when surface hardness matters.
Borofloat 33 vs JGS1: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all glass grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all glass grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Compressive Strength
Flexural Strength
Shear Strength
Fracture Toughness (K_IC)
Hardness, Vickers
Hardness, Knoop
Same in both: Elongation at Break 0% · Hardness, Mohs 6
Physical
Density and transition temperatures.
Density
Refractive Index
Light Transmission
Melting Point (Solidus)
Same in both: Porosity 0%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Same in both: Dielectric Strength 30 kV/mm762 V/mil
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Polishability
Sintering / Firing Temperature
Same in both: Machinability 12 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every glass grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Borofloat 33 | JGS1 |
|---|---|---|
| Default condition | Annealed Glass | — |
| Relative cost | $$ Standard | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Borofloat 33 vs JGS1 — frequently asked
Is JGS1 stronger than Borofloat 33?
Yes. JGS1 has a typical tensile strength of 50 MPa (7.25 ksi) against 35 MPa (5.08 ksi) for Borofloat 33 — about 43% more.
Which is cheaper, Borofloat 33 or JGS1?
Borofloat 33 is the lower-cost material: it sits in the standard tier ($$) while JGS1 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
When should I choose Borofloat 33 over JGS1?
Pick Borofloat 33 when cost is the deciding factor. Pick JGS1 when strength drives the design, or when surface hardness matters.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Borofloat 33 and JGS1 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.