Copper Alloy C74000 vs C74400
Copper Alloy · grade comparison
Copper Alloy C74000 and C74400 are both copper alloy grades. C74400 is the stronger of the two: yield strength 440 MPa (63.8 ksi) against 380 MPa (55.1 ksi) for C74000, about 16% more; tensile strength follows at 515 MPa (74.7 ksi) vs 470 MPa (68.2 ksi). C74000 is harder — 155 HV against 145 HV for C74400 — which matters for wear surfaces and threads. On the shop floor, C74400 forms better (very good vs good).
C74000Choose it when surface hardness matters.
C74400Choose it when strength drives the design.
C74000 vs C74400: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all copper alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Shear Strength
Hardness, Brinell
Hardness, Vickers
Same in both: Shear Modulus 46 GPa6.7 Msi · Bulk Modulus 130 GPa18.9 Msi · Poisson's Ratio 0.34 · Elongation at Break 12% · Fatigue Strength (Endurance Limit) 200 MPa29 ksi · Hardness, Rockwell B 75 HRB
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 45 W/m·K26 BTU/hr·ft·°F · Specific Heat Capacity 377 J/kg·K0.09 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 16.2 µm/m·K9 µin/in·°F · Latent Heat of Fusion 200 J/g86 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -200°C-328 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 62 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Polishability
Same in both: Machinability Rating (AISI 1212 = 100 %) 20% · Brazeability / Solderability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 14.3 MN·m/kg
Strength versus weight
Yield strength against density for every copper alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C74000 | C74400 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 4 finishes: Copper Plating, Electroless Nickel (EN), Gold Plating, Silver Plating.
C74000 vs C74400 — frequently asked
Is C74400 stronger than C74000?
Yes. C74400 has a typical yield strength of 440 MPa (63.8 ksi) against 380 MPa (55.1 ksi) for C74000 — about 16% more. Tensile strength is 515 MPa (74.7 ksi) vs 470 MPa (68.2 ksi).
Which is cheaper, C74000 or C74400?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, C74000 or C74400?
C74000, by a small margin. Both rate poor for machinability — 30/100 against 25/100 for C74400.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C74000 and C74400 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.