FR-6 vs G-3
Composite · grade comparison
FR-6 and G-3 are both composite grades. G-3 is the stronger of the two: tensile strength 250 MPa (36.3 ksi) against 85 MPa (12.3 ksi) for FR-6, about 194% more. G-3 is the more ductile: elongation 1.5% versus 1.2% for FR-6. G-3 is stiffer (18 GPa vs 10 GPa).
G-3Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
FR-6 vs G-3: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Izod Impact, Notched
Hardness, Rockwell M
Physical
Density and transition temperatures.
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Same in both: Density 1.85 g/cm³0.07 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Min Service Temperature
Heat Deflection Temp. @ 1.8 MPa
Limiting Oxygen Index
Same in both: Specific Heat Capacity 1,150 J/kg·K0.27 BTU/lb·°F · Max Service Temperature (continuous) 130°C266 °F · Max Service Temperature (short-term) 180°C356 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Surface Resistivity
Comparative Tracking Index (CTI)
Same in both: Dielectric Strength 14 kV/mm356 V/mil
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | FR-6 | G-3 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | — | — |
| Best machined surface | — | — |
FR-6 vs G-3 — frequently asked
Is G-3 stronger than FR-6?
Yes. G-3 has a typical tensile strength of 250 MPa (36.3 ksi) against 85 MPa (12.3 ksi) for FR-6 — about 194% more.
Which is cheaper, FR-6 or G-3?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose FR-6 over G-3?
Pick G-3 when strength drives the design, or when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in FR-6 and G-3 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.