AS4D vs T800H
Composite · grade comparison
AS4D and T800H are both composite grades. T800H is the stronger of the two: tensile strength 5,490 MPa (796 ksi) against 4,480 MPa (650 ksi) for AS4D, about 23% more. T800H is stiffer (294 GPa vs 245 GPa) and T800H conducts heat better (35 W/m·K vs 6.8 W/m·K).
T800HChoose it when strength drives the design.
AS4D vs T800H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all composite grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Elongation at Break
Compressive Strength
Physical
Density and transition temperatures.
Density
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Specific Heat Capacity 750 J/kg·K0.18 BTU/lb·°F · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -269°C-452 °F · Max Service Temperature (short-term) 500°C932 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Volume Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 0%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every composite grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | AS4D | T800H |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
AS4D vs T800H — frequently asked
Is T800H stronger than AS4D?
Yes. T800H has a typical tensile strength of 5,490 MPa (796 ksi) against 4,480 MPa (650 ksi) for AS4D — about 23% more.
Which is cheaper, AS4D or T800H?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
When should I choose AS4D over T800H?
Pick T800H when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in AS4D and T800H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.