Aluminum 6060 vs 6110
Aluminum · grade comparison
Aluminum 6060 and 6110 are both aluminum grades, both multipurpose al. 6110 is the stronger of the two: yield strength 360 MPa (52.2 ksi) against 170 MPa (24.7 ksi) for 6060, about 112% more; tensile strength follows at 390 MPa (56.6 ksi) vs 215 MPa (31.2 ksi). 6110 is harder — 118 HB against 75 HB for 6060 — which matters for wear surfaces and threads. 6060 conducts heat better (200 W/m·K vs 160 W/m·K). On the shop floor, 6110 machines more easily (very good vs good), 6060 welds better (excellent vs good), and 6060 forms better (good vs fair).
6060Choose it when it will be welded, or when cost is the deciding factor.
6110Choose it when strength drives the design, or when surface hardness matters.
6060 vs 6110: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Vickers
Same in both: Poisson's Ratio 0.33 · Elongation at Break 12%
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Min Service Temperature
Same in both: Thermal Expansion (CTE, 20–100 °C) 23.4 µm/m·K13 µin/in·°F · Max Service Temperature (continuous) 150°C302 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Machinability Rating (AISI 1212 = 100 %)
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 6060 | 6110 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | 0.5 mm | 0.5 mm |
| Best machined surface | Ra 0.8 µm | Ra 0.8 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 16 finishes: Anodizing Type II, Cerakote, Chem Film (Alodine), DLC, E-Coating, Electroless Nickel (EN), Electropolishing, Epoxy Coating, Gold Plating, Hard Anodize Type III w/ PTFE, Hard Anodizing Type III, Nickel Plating and 4 more.
6060 vs 6110 — frequently asked
Is 6110 stronger than 6060?
Yes. 6110 has a typical yield strength of 360 MPa (52.2 ksi) against 170 MPa (24.7 ksi) for 6060 — about 112% more. Tensile strength is 390 MPa (56.6 ksi) vs 215 MPa (31.2 ksi).
Which is cheaper, 6060 or 6110?
6060 is the lower-cost material: it sits in the budget tier ($) while 6110 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 6060 or 6110?
6110. Its machinability rates very good (72/100) against good (55/100) for 6060; for welding the order is 6060 first (excellent, 90/100) then 6110 (good, 58/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 6060 and 6110 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.