Aluminum 2017A vs 2A17
Aluminum · grade comparison
Aluminum 2017A and 2A17 are both aluminum grades. 2A17 is the stronger of the two: yield strength 320 MPa (46.4 ksi) against 260 MPa (37.7 ksi) for 2017A, about 23% more; tensile strength follows at 440 MPa (63.8 ksi) vs 410 MPa (59.5 ksi). In exchange, 2017A is the more ductile: elongation 14% versus 9% for 2A17, and 2A17 is harder (120 HB vs 110 HB). 2A17 runs hotter in service (250°C vs 120°C continuous). On the shop floor, 2A17 welds better (good vs poor) and 2017A sits in a lower cost tier (premium, $$$) than 2A17 (high, $$$$).
2017AChoose it when the part is bent, formed or impact-loaded, or when cost is the deciding factor.
2A17Choose it when strength drives the design, or when the part sees heat.
2017A vs 2A17: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Reduction in Area
Same in both: Shear Modulus 27 GPa3.9 Msi · Poisson's Ratio 0.33 · Shear Strength 260 MPa37.7 ksi · Fatigue Strength (Endurance Limit) 125 MPa18.1 ksi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.69 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 25 / 100 · Brazeability / Solderability 15 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 2017A | 2A17 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Cerakote | Yes | — |
| Chem Film (Alodine) | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| Electropolishing | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
2017A vs 2A17 — frequently asked
Is 2A17 stronger than 2017A?
Yes. 2A17 has a typical yield strength of 320 MPa (46.4 ksi) against 260 MPa (37.7 ksi) for 2017A — about 23% more. Tensile strength is 440 MPa (63.8 ksi) vs 410 MPa (59.5 ksi).
Which is cheaper, 2017A or 2A17?
2017A is the lower-cost material: it sits in the premium tier ($$$) while 2A17 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 2017A or 2A17?
2A17. Its weldability rates good (58/100) against poor (20/100) for 2017A.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2017A and 2A17 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.