Aluminum 2017A vs 2195
Aluminum · grade comparison
Aluminum 2017A and 2195 are both aluminum grades. 2195 is the stronger of the two: yield strength 550 MPa (79.8 ksi) against 260 MPa (37.7 ksi) for 2017A, about 112% more; tensile strength follows at 590 MPa (85.6 ksi) vs 410 MPa (59.5 ksi). In exchange, 2017A is the more ductile: elongation 14% versus 9% for 2195, and 2195 is harder (160 HB vs 110 HB). 2195 runs hotter in service (150°C vs 120°C continuous) and 2017A conducts heat better (134 W/m·K vs 115 W/m·K). On the shop floor, 2017A machines more easily (very good vs good), 2195 welds better (good vs poor), and 2017A sits in a lower cost tier (premium, $$$) than 2195 (high, $$$$).
2017AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
2195Choose it when strength drives the design, or when the part sees heat.
2017A vs 2195: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Reduction in Area
Same in both: Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 390 J/g168 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Castability 25 / 100 · Brazeability / Solderability 15 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 2017A | 2195 |
|---|---|---|
| Default condition | — | T8 |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.8 mm | 0.5 mm |
| Best machined surface | Ra 0.8 µm | Ra 0.8 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 16 finishes: Anodizing Type II, Cerakote, Chem Film (Alodine), DLC, E-Coating, Electroless Nickel (EN), Electropolishing, Epoxy Coating, Gold Plating, Hard Anodize Type III w/ PTFE, Hard Anodizing Type III, Nickel Plating and 4 more.
2017A vs 2195 — frequently asked
Is 2195 stronger than 2017A?
Yes. 2195 has a typical yield strength of 550 MPa (79.8 ksi) against 260 MPa (37.7 ksi) for 2017A — about 112% more. Tensile strength is 590 MPa (85.6 ksi) vs 410 MPa (59.5 ksi).
Which is cheaper, 2017A or 2195?
2017A is the lower-cost material: it sits in the premium tier ($$$) while 2195 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 2017A or 2195?
2017A. Its machinability rates very good (75/100) against good (58/100) for 2195; for welding the order is 2195 first (good, 62/100) then 2017A (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2017A and 2195 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.