Aluminum 2007 vs 2017A
Aluminum · grade comparison
Aluminum 2007 and 2017A are both aluminum grades, both high strength al. 2007 is the stronger of the two: yield strength 300 MPa (43.5 ksi) against 260 MPa (37.7 ksi) for 2017A, about 15% more. In exchange, 2017A is the more ductile: elongation 14% versus 10% for 2007. 2017A conducts electricity better (34 % IACS vs 30 % IACS). On the shop floor, 2007 machines more easily (excellent vs very good).
2007Choose it when strength drives the design, or when the part is machined in volume.
2017AChoose it when the part is bent, formed or impact-loaded.
2007 vs 2017A: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell B
Compressive Strength
Hardness, Vickers
Same in both: Shear Modulus 27 GPa3.9 Msi · Poisson's Ratio 0.33 · Fatigue Strength (Endurance Limit) 125 MPa18.1 ksi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Same in both: Thermal Expansion (CTE, 20–100 °C) 23 µm/m·K12.8 µin/in·°F · Latent Heat of Fusion 390 J/g168 BTU/lb · Max Service Temperature (continuous) 120°C248 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Castability 25 / 100 · Brazeability / Solderability 15 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 2007 | 2017A |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | 0.5 mm | 0.8 mm |
| Best machined surface | Ra 0.8 µm | Ra 0.8 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 16 finishes: Anodizing Type II, Cerakote, Chem Film (Alodine), DLC, E-Coating, Electroless Nickel (EN), Electropolishing, Epoxy Coating, Gold Plating, Hard Anodize Type III w/ PTFE, Hard Anodizing Type III, Nickel Plating and 4 more.
2007 vs 2017A — frequently asked
Is 2007 stronger than 2017A?
Yes. 2007 has a typical yield strength of 300 MPa (43.5 ksi) against 260 MPa (37.7 ksi) for 2017A — about 15% more. Tensile strength is 390 MPa (56.6 ksi) vs 410 MPa (59.5 ksi).
Which is cheaper, 2007 or 2017A?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 2007 or 2017A?
2007. Its machinability rates excellent (95/100) against very good (75/100) for 2017A; for welding the order is 2017A first (poor, 20/100) then 2007 (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2007 and 2017A side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.