Aluminum 2017A vs 2050
Aluminum · grade comparison
Aluminum 2017A and 2050 are both aluminum grades. 2050 is the stronger of the two: yield strength 495 MPa (71.8 ksi) against 260 MPa (37.7 ksi) for 2017A, about 90% more; tensile strength follows at 530 MPa (76.9 ksi) vs 410 MPa (59.5 ksi). In exchange, 2017A is the more ductile: elongation 14% versus 9% for 2050, and 2050 is harder (150 HB vs 110 HB). 2050 is lighter (2.7 g/cm³ vs 2.79 g/cm³ for 2017A) and 2050 is stiffer (76.5 GPa vs 72.5 GPa). On the shop floor, 2050 welds better (fair vs poor) and 2017A sits in a lower cost tier (premium, $$$) than 2050 (high, $$$$).
2017AChoose it when the part is bent, formed or impact-loaded, or when cost is the deciding factor.
2050Choose it when strength drives the design, or when weight is the constraint.
2017A vs 2050: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Bulk Modulus 75 GPa10.9 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 390 J/g168 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Same in both: Brazeability / Solderability 15 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 2017A | 2050 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Cerakote | Yes | — |
| Chem Film (Alodine) | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| Electropolishing | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
2017A vs 2050 — frequently asked
Is 2050 stronger than 2017A?
Yes. 2050 has a typical yield strength of 495 MPa (71.8 ksi) against 260 MPa (37.7 ksi) for 2017A — about 90% more. Tensile strength is 530 MPa (76.9 ksi) vs 410 MPa (59.5 ksi).
Which is cheaper, 2017A or 2050?
2017A is the lower-cost material: it sits in the premium tier ($$$) while 2050 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 2017A or 2050?
2017A, by a small margin. Both rate very good for machinability — 75/100 against 70/100 for 2050; for welding the order is 2050 first (fair, 35/100) then 2017A (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2017A and 2050 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.