Aluminum 2007 vs 2A25
Aluminum · grade comparison
Aluminum 2007 and 2A25 are both aluminum grades. 2A25 is the stronger of the two: yield strength 395 MPa (57.3 ksi) against 300 MPa (43.5 ksi) for 2007, about 32% more; tensile strength follows at 450 MPa (65.3 ksi) vs 390 MPa (56.6 ksi). In exchange, 2007 is the more ductile: elongation 10% versus 9% for 2A25, and 2A25 is harder (130 HB vs 115 HB). 2A25 runs hotter in service (150°C vs 120°C continuous) and 2A25 conducts heat better (155 W/m·K vs 135 W/m·K). On the shop floor, 2007 machines more easily (excellent vs very good) and 2A25 welds better (25 vs 15 out of 100).
2007Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
2A25Choose it when strength drives the design, or when the part sees heat.
2007 vs 2A25: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell B
Reduction in Area
Compressive Strength
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 72 GPa10.4 Msi · Shear Modulus 27 GPa3.9 Msi · Poisson's Ratio 0.33 · Fatigue Strength (Endurance Limit) 125 MPa18.1 ksi
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Polishability
Same in both: Brazeability / Solderability 15 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 200 MJ/kg85,985 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 2007 | 2A25 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$ Premium |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Cerakote | Yes | — |
| Chem Film (Alodine) | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| Electropolishing | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
2007 vs 2A25 — frequently asked
Is 2A25 stronger than 2007?
Yes. 2A25 has a typical yield strength of 395 MPa (57.3 ksi) against 300 MPa (43.5 ksi) for 2007 — about 32% more. Tensile strength is 450 MPa (65.3 ksi) vs 390 MPa (56.6 ksi).
Which is cheaper, 2007 or 2A25?
Both sit in the same relative cost tier ($$$, premium); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 2007 or 2A25?
2007. Its machinability rates excellent (95/100) against very good (70/100) for 2A25; for welding the order is 2A25 first (poor, 25/100) then 2007 (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2007 and 2A25 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.