Aluminum 2007 vs 2196
Aluminum · grade comparison
Aluminum 2007 and 2196 are both aluminum grades. 2196 is the stronger of the two: yield strength 560 MPa (81.2 ksi) against 300 MPa (43.5 ksi) for 2007, about 87% more; tensile strength follows at 600 MPa (87 ksi) vs 390 MPa (56.6 ksi). In exchange, 2007 is the more ductile: elongation 10% versus 8% for 2196, and 2196 is harder (150 HB vs 115 HB). 2196 is lighter (2.63 g/cm³ vs 2.85 g/cm³ for 2007) and 2196 is stiffer (78 GPa vs 72 GPa). On the shop floor, 2007 machines more easily (excellent vs good), 2196 welds better (fair vs poor), and 2007 sits in a lower cost tier (premium, $$$) than 2196 (high, $$$$).
2007Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
2196Choose it when strength drives the design, or when weight is the constraint.
2007 vs 2196: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell B
Compressive Strength
Same in both: Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 390 J/g168 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 32
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 2007 | 2196 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Cerakote | Yes | — |
| Chem Film (Alodine) | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| Electropolishing | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
2007 vs 2196 — frequently asked
Is 2196 stronger than 2007?
Yes. 2196 has a typical yield strength of 560 MPa (81.2 ksi) against 300 MPa (43.5 ksi) for 2007 — about 87% more. Tensile strength is 600 MPa (87 ksi) vs 390 MPa (56.6 ksi).
Which is cheaper, 2007 or 2196?
2007 is the lower-cost material: it sits in the premium tier ($$$) while 2196 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 2007 or 2196?
2007. Its machinability rates excellent (95/100) against good (65/100) for 2196; for welding the order is 2196 first (fair, 40/100) then 2007 (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2007 and 2196 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.