Aluminum 2007 vs 2139
Aluminum · grade comparison
Aluminum 2007 and 2139 are both aluminum grades. 2139 is the stronger of the two: yield strength 450 MPa (65.3 ksi) against 300 MPa (43.5 ksi) for 2007, about 50% more; tensile strength follows at 485 MPa (70.3 ksi) vs 390 MPa (56.6 ksi). 2139 is harder — 135 HB against 115 HB for 2007 — which matters for wear surfaces and threads. 2139 runs hotter in service (150°C vs 120°C continuous) and 2139 conducts heat better (150 W/m·K vs 135 W/m·K). On the shop floor, 2007 machines more easily (excellent vs very good) and 2007 sits in a lower cost tier (premium, $$$) than 2139 (high, $$$$).
2007Choose it when the part is machined in volume, or when cost is the deciding factor.
2139Choose it when strength drives the design, or when surface hardness matters.
2007 vs 2139: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell B
Compressive Strength
Same in both: Elastic (Young's) Modulus 72 GPa10.4 Msi · Shear Modulus 27 GPa3.9 Msi · Bulk Modulus 71 GPa10.3 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 2.85 g/cm³0.1 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Latent Heat of Fusion 390 J/g168 BTU/lb · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Castability
Polishability
Same in both: Formability (cold) 25 / 100 · Brazeability / Solderability 15 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Carbon (primary production) 12.5 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 25.3 MN·m/kg
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 2007 | 2139 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | — | — |
| Relative cost | $$$ Premium | $$$$ High |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Anodizing Type II | Yes | — |
| Cerakote | Yes | — |
| Chem Film (Alodine) | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| Electropolishing | Yes | — |
| Hard Anodize Type III w/ PTFE | Yes | — |
| Hard Anodizing Type III | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
They share 4 finishes: Electroless Nickel (EN), Epoxy Coating, Gold Plating, Silver Plating.
2007 vs 2139 — frequently asked
Is 2139 stronger than 2007?
Yes. 2139 has a typical yield strength of 450 MPa (65.3 ksi) against 300 MPa (43.5 ksi) for 2007 — about 50% more. Tensile strength is 485 MPa (70.3 ksi) vs 390 MPa (56.6 ksi).
Which is cheaper, 2007 or 2139?
2007 is the lower-cost material: it sits in the premium tier ($$$) while 2139 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 2007 or 2139?
2007. Its machinability rates excellent (95/100) against very good (72/100) for 2139; for welding the order is 2139 first (poor, 20/100) then 2007 (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 2007 and 2139 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.