Aluminum 1070 vs 1145
Aluminum · grade comparison
Aluminum 1070 and 1145 are both aluminum grades. 1145 is the stronger of the two: yield strength 150 MPa (21.8 ksi) against 25 MPa (3.63 ksi) for 1070, about 6.0 times as much; tensile strength follows at 165 MPa (23.9 ksi) vs 68 MPa (9.86 ksi). In exchange, 1070 is the more ductile: elongation 43% versus 4% for 1145, and 1145 is harder (42 HB vs 19 HB). 1070 runs hotter in service (150°C vs 100°C continuous).
1070Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
1145Choose it when strength drives the design.
1070 vs 1145: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all aluminum grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 69 GPa10 Msi · Shear Modulus 26 GPa3.8 Msi · Poisson's Ratio 0.33
Physical
Density and transition temperatures.
Density
Same in both: Melting Point (Solidus) 646°C1,195 °F · Liquidus Temperature 657°C1,215 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 900 J/kg·K0.21 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 23.6 µm/m·K13.1 µin/in·°F · Latent Heat of Fusion 397 J/g171 BTU/lb · Min Service Temperature -270°C-454 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.84 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Castability
Same in both: Machinability Rating (AISI 1212 = 100 %) 45%
Sustainability
Primary-production footprint per kilogram.
Typical Recycled Content
Same in both: Embodied Energy (primary production) 205 MJ/kg88,134 BTU/lb · Embodied Carbon (primary production) 12.5 kg CO₂/kg · Embodied Water 1,200 L/kg144 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every aluminum grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1070 | 1145 |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | — | — |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| DLC | Yes | — |
Both are offered for Sheet metal. They share 15 finishes: Anodizing Type II, Cerakote, Chem Film (Alodine), E-Coating, Electroless Nickel (EN), Electropolishing, Epoxy Coating, Gold Plating, Hard Anodize Type III w/ PTFE, Hard Anodizing Type III, Nickel Plating, PTFE Coating and 3 more.
1070 vs 1145 — frequently asked
Is 1145 stronger than 1070?
Yes. 1145 has a typical yield strength of 150 MPa (21.8 ksi) against 25 MPa (3.63 ksi) for 1070 — about 6.0 times as much. Tensile strength is 165 MPa (23.9 ksi) vs 68 MPa (9.86 ksi).
Which is cheaper, 1070 or 1145?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1070 or 1145?
1070. Its machinability rates fair (35/100) against poor (30/100) for 1145.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1070 and 1145 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.