Solder & Low-Melting Alloy Wood's Metal F-AGED
Heat-treated state
also Cerrobend
F-AGED = cast, room-temperature aged ≥24 h
Use when dimensional stability matters (dies, holding fixtures): the slight post-cast growth of the Bi phase has finished after about a day.
Values for the F-AGED condition
Other Wood's Metal tempers and conditions
Wood's Metal is listed in 2 conditions; see the grade overview at Wood's Metal.
- F
- F-AGED
Compare all 2 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
FDefault As fabricated | Default condition: melted in hot water/oil bath and poured into the cavity or fusible plug body. | 25 | 42 | 25 | 11 HB | 3 % IACS |
F-AGEDThis page Cast, room-temperature aged ≥24 h | Use when dimensional stability matters (dies, holding fixtures): the slight post-cast growth of the Bi phase has finished after about a day. | 30 | 48 | 18 | 13 HB | 3 % IACS |
What is Wood's Metal F-AGED?
Wood's Metal F-AGED is Wood's Metal heat treated to F-AGED — use when dimensional stability matters (dies, holding fixtures): the slight post-cast growth of the Bi phase has finished after about a day. Wood's Metal F-AGED has a yield strength of 30 MPa (4.35 ksi) and a tensile strength of 48 MPa (6.96 ksi) — stronger than 61% of solder & low-melting alloy grades. Elongation at break is 18% and the elastic modulus is 10 GPa (1.45 Msi). Wood's Metal F-AGED has a density of 9.7 g/cm³ (0.35 lb/in³), heavier than 70% of solder & low-melting alloy grades. It melts at 70°C (158 °F). F is the default condition FabDigit quotes; F-AGED is available on request or by drawing note.
Advantages
- Low embodied carbon — 4 kg CO₂/kg, better than 80% of solder & low-melting alloy grades
Limitations
- Poor heat conductor — 13 W/m·K (7.51 BTU/hr·ft·°F), worse than 99% of solder & low-melting alloy grades
- Low stiffness — 10 GPa (1.45 Msi), worse than 98% of solder & low-melting alloy grades
- Low electrical conductivity — 3 % IACS, worse than 98% of solder & low-melting alloy grades
- Limited service temperature — 40°C (104 °F), worse than 97% of solder & low-melting alloy grades
- Limited formability — 30/100, worse than 88% of solder & low-melting alloy grades
Wood's Metal F-AGED properties
Typical room-temperature values for Wood's Metal F-AGED; 19 are specific to this condition. Other listed values are Wood's Metal reference data and may not represent this condition. Bars are the position among solder & low-melting alloy grades.
Physical3
Wood's Metal F-AGED has a density of 9.7 g/cm³ (0.35 lb/in³), heavier than 70% of solder & low-melting alloy grades. It melts at 70°C (158 °F).
Mechanical13
Wood's Metal F-AGED has a yield strength of 30 MPa (4.35 ksi) and a tensile strength of 48 MPa (6.96 ksi) — stronger than 61% of solder & low-melting alloy grades. Elongation at break is 18% and the elastic modulus is 10 GPa (1.45 Msi).
Thermal6
Wood's Metal F-AGED is rated for continuous service to 40°C (104 °F). It conducts heat at 13 W/m·K (7.51 BTU/hr·ft·°F), worse than 99% of solder & low-melting alloy grades. Thermal expansion is 23 µm/m·K (12.8 µin/in·°F).
Electrical3
Wood's Metal F-AGED conducts electricity at 3 % IACS, worse than 98% of solder & low-melting alloy grades.
Chemical & Environmental3
Corrosion resistance is fair (38/100), worse than 90% of solder & low-melting alloy grades.
Sustainability3
Producing a kilogram of Wood's Metal F-AGED takes about 55 MJ of energy and emits 4 kg of CO₂ — less than 79% of solder & low-melting alloy grades. Typical recycled content is 40%.
Manufacturability8
Wood's Metal F-AGED's machinability is fair (40/100, better than 65% of solder & low-melting alloy grades); weldability poor (15/100); formability poor (30/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Wood's Metal F-AGED
Is Wood's Metal easy to machine?
Cuts easily but smears and can melt from cutting heat — use sharp HSS tools, high rake, flood coolant, and capture all chips as hazardous Pb/Cd waste.
Can Wood's Metal be welded?
Not weldable in the usual sense; joints are made by simply remelting the alloy at 70–100 °C in a water or oil bath.
Can Wood's Metal be formed, bent or molded?
Gravity or hand pour at 80–100 °C into silicone, plaster or metal moulds; near-zero shrinkage reproduces fine detail, and cast tube-bending cores are removed by hot-water melt-out.
What surface finishes work on Wood's Metal?
Too soft to polish or plate practically; surfaces tarnish grey, so leave as-cast and never use in food, skin or potable-water contact.
Wood's Metal chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Bieutectic base, gives near-zero solidification shrinkage | 49 – 51 | 50 |
| Pb | 25.5 – 27.5 | 26.7 |
| Sn | 12.5 – 14 | 13.3 |
| Cdtoxic; reason for RoHS/REACH restriction | 9.5 – 10.5 | 10 |
| impurities (Sb, Cu, Zn, Fe, As)total, typical commercial limit | ≤ 0.15 | — |
Wood's Metal F-AGED — frequently asked
What is Wood's Metal F-AGED used for?
Wood's Metal F-AGED is typically used for fire sprinkler fusible links, tube bending fill alloy, fusible safety plugs and pattern/mold making. In short: 70 °C melting fusible alloy; near-zero casting shrinkage; cd/Pb-bearing legacy grade.
What is the yield strength of Wood's Metal F-AGED?
Wood's Metal F-AGED has a typical yield strength of 30 MPa (4.35 ksi) and a tensile strength of 48 MPa (6.96 ksi) — stronger than 61% of solder & low-melting alloy grades. Strength varies by condition: see the 2 listed tempers.
Is Wood's Metal F-AGED easy to machine?
Not especially — machinability is rated fair (40/100, better than 65% of solder & low-melting alloy grades). Cuts easily but smears and can melt from cutting heat — use sharp HSS tools, high rake, flood coolant, and capture all chips as hazardous Pb/Cd waste.
Can Wood's Metal F-AGED be welded?
Not readily — weldability is rated poor (15/100). Not weldable in the usual sense; joints are made by simply remelting the alloy at 70–100 °C in a water or oil bath.
What surface finishes work on Wood's Metal F-AGED?
Too soft to polish or plate practically; surfaces tarnish grey, so leave as-cast and never use in food, skin or potable-water contact.
Can Wood's Metal F-AGED be formed, bent or molded?
Gravity or hand pour at 80–100 °C into silicone, plaster or metal moulds; near-zero shrinkage reproduces fine detail, and cast tube-bending cores are removed by hot-water melt-out.
What is the maximum service temperature of Wood's Metal F-AGED?
Wood's Metal F-AGED is rated for continuous use to about 40°C (104 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between Wood's Metal-F and Wood's Metal F-AGED?
F is the default condition — default condition: melted in hot water/oil bath and poured into the cavity or fusible plug body. F-AGED: use when dimensional stability matters (dies, holding fixtures): the slight post-cast growth of the Bi phase has finished after about a day. Yield strength is 25 MPa in F versus 30 MPa in F-AGED.
Sources
- ASM Handbook Vol. 2 — Properties and Selection: Nonferrous Alloys (Low-Melting/Fusible Alloys) — ASM International (1990)
- Cerrobend / fusible alloy technical data (70 °C eutectic) — fusible-alloy producers (2020)
- CRC Handbook of Chemistry and Physics — low-melting alloy data — CRC Press (2021)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.