Precious Metal Gold 24K-H02
Supply condition
also Pure Gold
H02 = half hard
Choose when soft gold sheet/wire needs some spring-back and handling stiffness while still being formable.
Values for the H02 condition
Other Gold 24K tempers and conditions
Gold 24K is listed in 4 conditions; see the grade overview at Gold 24K.
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
As fabricated | Condition of poured bars, grain and investment castings before working; coarse grain, slightly lower strength than wrought annealed. | 28 | 105 | 30 | 24 HB | 71 % IACS |
ODefault Annealed | Default stock condition for foil, bonding wire, sheet and bullion working — maximum ductility for beating, drawing and bonding. | 30 | 125 | 45 | 25 HB | 71 % IACS |
H02This page Half hard | Choose when soft gold sheet/wire needs some spring-back and handling stiffness while still being formable. | 130 | 170 | 15 | 43 HB | 70.5 % IACS |
Full hard | Maximum strength condition for as-drawn fine wire, contacts and springs; anneals back to soft above ~200 °C. | 205 | 220 | 4 | 55 HB | 70 % IACS |
What is Gold 24K-H02?
Gold 24K-H02 is Gold 24K supplied in the H02 condition — choose when soft gold sheet/wire needs some spring-back and handling stiffness while still being formable. Gold 24K-H02 has a yield strength of 130 MPa (18.9 ksi) and a tensile strength of 170 MPa (24.7 ksi) — weaker than 72% of precious metal grades. Elongation at break is 15% and the elastic modulus is 78 GPa (11.3 Msi). Gold 24K-H02 has a density of 19.32 g/cm³ (0.698 lb/in³), heavier than 91% of precious metal grades. It melts at 1,064°C (1,948 °F). O is the default condition FabDigit quotes; H02 is available on request or by drawing note.
Advantages
- Good corrosion resistance — 100/100, better than 98% of precious metal grades
- Readily welded — 80/100, better than 87% of precious metal grades
- Polishes to a fine finish — 95/100, better than 86% of precious metal grades
- Conducts heat well — 315 W/m·K (182 BTU/hr·ft·°F), better than 76% of precious metal grades
- High electrical conductivity — 70.5 % IACS, better than 75% of precious metal grades
Limitations
- Limited service temperature — 120°C (248 °F), worse than 100% of precious metal grades
- High embodied carbon — 25,000 kg CO₂/kg, worse than 99% of precious metal grades
- Heavy — 19.32 g/cm³ (0.698 lb/in³), worse than 91% of precious metal grades
- Low stiffness — 78 GPa (11.3 Msi), worse than 90% of precious metal grades
- Limited ductility — 15%, worse than 86% of precious metal grades
Gold 24K-H02 properties
Typical room-temperature values for Gold 24K-H02; 18 are specific to this condition. Other listed values are Gold 24K reference data and may not represent this condition. Bars are the position among precious metal grades.
Physical3
Gold 24K-H02 has a density of 19.32 g/cm³ (0.698 lb/in³), heavier than 91% of precious metal grades. It melts at 1,064°C (1,948 °F).
Mechanical11
Gold 24K-H02 has a yield strength of 130 MPa (18.9 ksi) and a tensile strength of 170 MPa (24.7 ksi) — weaker than 72% of precious metal grades. Elongation at break is 15% and the elastic modulus is 78 GPa (11.3 Msi).
Thermal6
Gold 24K-H02 is rated for continuous service to 120°C (248 °F). It conducts heat at 315 W/m·K (182 BTU/hr·ft·°F), better than 76% of precious metal grades. Thermal expansion is 14.2 µm/m·K (7.89 µin/in·°F).
Electrical3
Gold 24K-H02 conducts electricity at 70.5 % IACS, better than 75% of precious metal grades.
Chemical & Environmental3
Corrosion resistance is excellent (100/100), better than 98% of precious metal grades.
Sustainability4
Producing a kilogram of Gold 24K-H02 takes about 260,000 MJ of energy and emits 25,000 kg of CO₂ — more than 98% of precious metal grades. Typical recycled content is 28%.
Manufacturability8
Gold 24K-H02's machinability is fair (50/100, better than 74% of precious metal grades); weldability very good (80/100); formability very good (70/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Gold 24K-H02
Is Gold 24K easy to machine?
Very gummy and soft — use sharp positive-rake carbide or diamond tools, high speed, light feed, no built-up edge; single-point diamond turning gives optical mirror finishes; always collect swarf for refining.
Can Gold 24K be welded?
Excellent oxide-free laser, micro-TIG and torch welding with pure gold filler; avoid contamination by Pb, Bi, Hg or solder residues which cause hot cracking.
Can Gold 24K be formed, bent or molded?
Unlimited cold formability — rolls to <0.1 µm leaf, deep draws and coins easily; anneal 500–700 °C in air (no protective atmosphere needed) to reset work hardening.
What surface finishes work on Gold 24K?
Polishes to a mirror with fine alumina/diamond compound but scratches easily; no anodizing — hard-wear surfaces are protected with rhodium or hard-gold (Au-Co/Au-Ni) electroplate.
Gold 24K chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Agtypical residual from refining | ≤ 0.01 | 0 |
| Cu | ≤ 0.01 | 0 |
| Fe | ≤ 0 | 0 |
| Pbkept very low — embrittles gold | ≤ 0 | |
| Biembrittling impurity | ≤ 0 | |
| Pd+Ptcombined PGM residuals | ≤ 0.01 | |
| Total impuritiesfor 999.9 fine; ≤0.1 % for 999 fine per GB/T 4134 | ≤ 0.01 | 0.01 |
| AuAu9999 fine gold; Au999 (99.9 min) also standard commercial purity | ≥ 99.99 (balance) |
Gold 24K-H02 — frequently asked
What is Gold 24K-H02 used for?
Gold 24K-H02 is typically used for bullion bars and coins, semiconductor bonding wire, sputtering and evaporation targets, gold leaf and foil, electrical contact and connector plating stock and 24K fine jewelry. In short: pure investment-grade gold.
What is the yield strength of Gold 24K-H02?
Gold 24K-H02 has a typical yield strength of 130 MPa (18.9 ksi) and a tensile strength of 170 MPa (24.7 ksi) — weaker than 72% of precious metal grades. Strength varies by condition: see the 4 listed tempers.
Is Gold 24K-H02 easy to machine?
Reasonably — machinability is rated fair (50/100, better than 74% of precious metal grades). Very gummy and soft — use sharp positive-rake carbide or diamond tools, high speed, light feed, no built-up edge; single-point diamond turning gives optical mirror finishes; always collect swarf for refining.
Can Gold 24K-H02 be welded?
Yes — weldability is rated very good (80/100). Excellent oxide-free laser, micro-TIG and torch welding with pure gold filler; avoid contamination by Pb, Bi, Hg or solder residues which cause hot cracking.
What surface finishes work on Gold 24K-H02?
Polishes to a mirror with fine alumina/diamond compound but scratches easily; no anodizing — hard-wear surfaces are protected with rhodium or hard-gold (Au-Co/Au-Ni) electroplate.
Can Gold 24K-H02 be formed, bent or molded?
Unlimited cold formability — rolls to <0.1 µm leaf, deep draws and coins easily; anneal 500–700 °C in air (no protective atmosphere needed) to reset work hardening.
What is the maximum service temperature of Gold 24K-H02?
Gold 24K-H02 is rated for continuous use to about 120°C (248 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between Gold 24K-O and Gold 24K-H04?
O is the default condition — default stock condition for foil, bonding wire, sheet and bullion working — maximum ductility for beating, drawing and bonding. H04: maximum strength condition for as-drawn fine wire, contacts and springs; anneals back to soft above ~200 °C. Yield strength is 30 MPa in O versus 205 MPa in H04.
Sources
- ASTM B562 — Standard Specification for Refined Gold — ASTM International (2020)
- GB/T 4134 (Gold Ingots) — SAC / (2015)
- ASM Handbook Vol. 2 — Properties and Selection: Nonferrous Alloys and Special-Purpose Materials (Precious Metals) — ASM International (1990)
- CRC Handbook of Chemistry and Physics, Properties of the Elements — CRC Press (2022)
- Gold Bulletin / World Gold Council technical data on pure gold properties and GHG intensity — World Gold Council (2023)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.