Titanium Grade 1 vs Ti Grade 16
Titanium · grade comparison
Titanium Grade 1 and Ti Grade 16 are both titanium grades. Ti Grade 16 is the stronger of the two: yield strength 380 MPa (55.1 ksi) against 220 MPa (31.9 ksi) for Grade 1, about 73% more; tensile strength follows at 460 MPa (66.7 ksi) vs 300 MPa (43.5 ksi). In exchange, Grade 1 is the more ductile: elongation 30% versus 26% for Ti Grade 16, and Ti Grade 16 is harder (150 HB vs 120 HB). Grade 1 conducts heat better (20 W/m·K vs 16.4 W/m·K). On the shop floor, Ti Grade 16 sits in a lower cost tier (high, $$$$) than Grade 1 (specialty, $$$$$).
Grade 1Choose it when the part is bent, formed or impact-loaded.
Ti Grade 16Choose it when strength drives the design, or when cost is the deciding factor.
Grade 1 vs Ti Grade 16: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Melting Point (Solidus)
Same in both: Density 4.51 g/cm³0.16 lb/in³ · Liquidus Temperature 1,670°C3,038 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Latent Heat of Fusion
Same in both: Specific Heat Capacity 523 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 8.6 µm/m·K4.8 µin/in·°F · Max Service Temperature (continuous) 300°C572 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Polishability
Same in both: Brazeability / Solderability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Grade 1 | Ti Grade 16 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 1 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Anodizing Type II | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
They share 1 finish: Plasma Spray.
Grade 1 vs Ti Grade 16 — frequently asked
Is Ti Grade 16 stronger than Grade 1?
Yes. Ti Grade 16 has a typical yield strength of 380 MPa (55.1 ksi) against 220 MPa (31.9 ksi) for Grade 1 — about 73% more. Tensile strength is 460 MPa (66.7 ksi) vs 300 MPa (43.5 ksi).
Which is cheaper, Grade 1 or Ti Grade 16?
Ti Grade 16 is the lower-cost material: it sits in the high tier ($$$$) while Grade 1 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
When should I choose Grade 1 over Ti Grade 16?
Pick Grade 1 when the part is bent, formed or impact-loaded. Pick Ti Grade 16 when strength drives the design, or when cost is the deciding factor.
Ready to make it?
Upload a CAD file and FabDigit prices the part in Grade 1 and Ti Grade 16 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.