Titanium Grade 1 vs Ti Grade 12
Titanium · grade comparison
Titanium Grade 1 and Ti Grade 12 are both titanium grades. Ti Grade 12 is the stronger of the two: yield strength 450 MPa (65.3 ksi) against 220 MPa (31.9 ksi) for Grade 1, about 105% more; tensile strength follows at 550 MPa (79.8 ksi) vs 300 MPa (43.5 ksi). In exchange, Grade 1 is the more ductile: elongation 30% versus 22% for Ti Grade 12, and Ti Grade 12 is harder (200 HB vs 120 HB). On the shop floor, Grade 1 machines more easily (fair vs poor) and Ti Grade 12 sits in a lower cost tier (high, $$$$) than Grade 1 (specialty, $$$$$).
Grade 1Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
Ti Grade 12Choose it when strength drives the design, or when cost is the deciding factor.
Grade 1 vs Ti Grade 12: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 103 GPa14.9 Msi · Bulk Modulus 110 GPa16 Msi · Poisson's Ratio 0.34
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 4.51 g/cm³0.16 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 35 / 100 · Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 22.8 MN·m/kg
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Grade 1 | Ti Grade 12 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | O | — |
| Relative cost | $$$$$ Specialty | $$$$ High |
| Min. machined wall | 1 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Anodizing Type II | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| Electropolishing | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
They share 1 finish: Plasma Spray.
Grade 1 vs Ti Grade 12 — frequently asked
Is Ti Grade 12 stronger than Grade 1?
Yes. Ti Grade 12 has a typical yield strength of 450 MPa (65.3 ksi) against 220 MPa (31.9 ksi) for Grade 1 — about 105% more. Tensile strength is 550 MPa (79.8 ksi) vs 300 MPa (43.5 ksi).
Which is cheaper, Grade 1 or Ti Grade 12?
Ti Grade 12 is the lower-cost material: it sits in the high tier ($$$$) while Grade 1 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Grade 1 or Ti Grade 12?
Grade 1. Its machinability rates fair (42/100) against poor (30/100) for Ti Grade 12; for welding the order is Grade 1 first (excellent, 90/100) then Ti Grade 12 (excellent, 85/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Grade 1 and Ti Grade 12 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.