Titanium C-4 vs ZTA15
Titanium · grade comparison
Titanium C-4 and ZTA15 are both titanium grades. ZTA15 is the stronger of the two: yield strength 850 MPa (123 ksi) against 530 MPa (76.9 ksi) for C-4, about 60% more; tensile strength follows at 940 MPa (136 ksi) vs 620 MPa (89.9 ksi). In exchange, C-4 is the more ductile: elongation 12% versus 9% for ZTA15, and ZTA15 is harder (310 HB vs 265 HB). ZTA15 is stiffer (113 GPa vs 104 GPa) and ZTA15 runs hotter in service (500°C vs 300°C continuous). On the shop floor, C-4 machines more easily (30 vs 18 out of 100) and C-4 welds better (excellent vs very good).
C-4Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
ZTA15Choose it when strength drives the design, or when the part sees heat.
C-4 vs ZTA15: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all titanium grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Bulk Modulus 110 GPa16 Msi · Reduction in Area 20%
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every titanium grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | C-4 | ZTA15 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 1 finish: Plasma Spray.
C-4 vs ZTA15 — frequently asked
Is ZTA15 stronger than C-4?
Yes. ZTA15 has a typical yield strength of 850 MPa (123 ksi) against 530 MPa (76.9 ksi) for C-4 — about 60% more. Tensile strength is 940 MPa (136 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, C-4 or ZTA15?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, C-4 or ZTA15?
C-4, by a small margin. Both rate poor for machinability — 30/100 against 18/100 for ZTA15; for welding the order is C-4 first (excellent, 85/100) then ZTA15 (very good, 75/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in C-4 and ZTA15 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.