Steel SCCrM1-QT vs SCCrM1 QT 30-35 HRC
Steel · SCCrM1 temper comparison
SCCrM1-QT and SCCrM1 QT 30-35 HRC are two conditions of the same steel grade, SCCrM1: QT (quenched and tempered) versus QT 30-35 HRC (quenched and low-temperature tempered). The chemistry is identical, so every difference below comes from the condition. SCCrM1 QT 30-35 HRC is the stronger of the two: yield strength 830 MPa (120 ksi) against 640 MPa (92.8 ksi) for SCCrM1-QT, about 30% more; tensile strength follows at 1,000 MPa (145 ksi) vs 830 MPa (120 ksi). In exchange, SCCrM1-QT is the more ductile: elongation 16% versus 12% for SCCrM1 QT 30-35 HRC, and SCCrM1 QT 30-35 HRC is harder (302 HB vs 240 HB). SCCrM1-QT runs hotter in service (400°C vs 350°C continuous). On the shop floor, SCCrM1-QT machines more easily (45 vs 35 out of 100) and SCCrM1-QT welds better (45 vs 35 out of 100).
SCCrM1-QTChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
SCCrM1 QT 30-35 HRCChoose it when strength drives the design.
SCCrM1-QT vs SCCrM1 QT 30-35 HRC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 650 MPa94.3 ksi · Shear Strength 500 MPa72.5 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.5 % IACS · Electrical Resistivity 2.3×10⁻⁷ Ω·m9.06 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 14 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Same in both: Formability (cold) 15 / 100 · Castability 65 / 100 · Brazeability / Solderability 55 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 85%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SCCrM1-QT vs SCCrM1 QT 30-35 HRC — frequently asked
Is SCCrM1 QT 30-35 HRC stronger than SCCrM1-QT?
Yes. SCCrM1 QT 30-35 HRC has a typical yield strength of 830 MPa (120 ksi) against 640 MPa (92.8 ksi) for SCCrM1-QT — about 30% more. Tensile strength is 1,000 MPa (145 ksi) vs 830 MPa (120 ksi).
Which condition does FabDigit quote by default, QT or QT 30-35 HRC?
QT is the default SCCrM1 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, SCCrM1-QT or SCCrM1 QT 30-35 HRC?
SCCrM1-QT, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for SCCrM1 QT 30-35 HRC; for welding the order is SCCrM1-QT first (fair, 45/100) then SCCrM1 QT 30-35 HRC (fair, 35/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in SCCrM1-QT and SCCrM1 QT 30-35 HRC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.