SCCrM1-A and SCCrM1-QT are two conditions of the same steel grade, SCCrM1: A (solution annealed) versus QT (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. SCCrM1-QT is the stronger of the two: yield strength 640 MPa (92.8 ksi) against 380 MPa (55.1 ksi) for SCCrM1-A, about 68% more; tensile strength follows at 830 MPa (120 ksi) vs 620 MPa (89.9 ksi). In exchange, SCCrM1-A is the more ductile: elongation 22% versus 16% for SCCrM1-QT, and SCCrM1-QT is harder (240 HB vs 175 HB). On the shop floor, SCCrM1-A machines more easily (good vs fair) and SCCrM1-A welds better (good vs fair).
SCCrM1-AChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
SCCrM1-QTChoose it when strength drives the design.
SCCrM1-A vs SCCrM1-QT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 650 MPa94.3 ksi · Shear Strength 500 MPa72.5 ksi · Fracture Toughness (K_IC) 75 MPa·√m68.3 ksi·√in · Hardness, Rockwell C 23 HRC
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.5 % IACS · Electrical Resistivity 2.3×10⁻⁷ Ω·m9.06 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 14 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Same in both: Formability (cold) 15 / 100 · Castability 65 / 100 · Brazeability / Solderability 55 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 85%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SCCrM1-A vs SCCrM1-QT — frequently asked
Is SCCrM1-QT stronger than SCCrM1-A?
Yes. SCCrM1-QT has a typical yield strength of 640 MPa (92.8 ksi) against 380 MPa (55.1 ksi) for SCCrM1-A — about 68% more. Tensile strength is 830 MPa (120 ksi) vs 620 MPa (89.9 ksi).
Which condition does FabDigit quote by default, A or QT?
QT is the default SCCrM1 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, SCCrM1-A or SCCrM1-QT?
SCCrM1-A. Its machinability rates good (60/100) against fair (45/100) for SCCrM1-QT; for welding the order is SCCrM1-A first (good, 55/100) then SCCrM1-QT (fair, 45/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in SCCrM1-A and SCCrM1-QT side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.