Steel S355J2W vs S700MC
Steel · grade comparison
Steel S355J2W and S700MC are both steel grades. S700MC is the stronger of the two: yield strength 740 MPa (107 ksi) against 380 MPa (55.1 ksi) for S355J2W, about 95% more; tensile strength follows at 810 MPa (117 ksi) vs 520 MPa (75.4 ksi). In exchange, S355J2W is the more ductile: elongation 24% versus 14% for S700MC, and S700MC is harder (245 HB vs 160 HB). S355J2W runs hotter in service (400°C vs 300°C continuous) and S355J2W conducts heat better (45 W/m·K vs 40 W/m·K). On the shop floor, S355J2W machines more easily (good vs fair) and S355J2W sits in a lower cost tier (budget, $) than S700MC (standard, $$).
S355J2WChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
S700MCChoose it when strength drives the design.
S355J2W vs S700MC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Reduction in Area 55%
Physical
Density and transition temperatures.
Melting Point (Solidus)
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Same in both: Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.8 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | S355J2W | S700MC |
|---|---|---|
| Sheet metal | — | Yes |
| Default condition | — | TMCP |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Black Oxide | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| E-Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
| Powder Coating | — | Yes |
| Tin Plating | — | Yes |
| Zinc Plating | — | Yes |
| Zinc-Flake (Dip-Spin) Coating | — | Yes |
| Zinc-Nickel Plating | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
S355J2W vs S700MC — frequently asked
Is S700MC stronger than S355J2W?
Yes. S700MC has a typical yield strength of 740 MPa (107 ksi) against 380 MPa (55.1 ksi) for S355J2W — about 95% more. Tensile strength is 810 MPa (117 ksi) vs 520 MPa (75.4 ksi).
Which is cheaper, S355J2W or S700MC?
S355J2W is the lower-cost material: it sits in the budget tier ($) while S700MC is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, S355J2W or S700MC?
S355J2W. Its machinability rates good (55/100) against fair (45/100) for S700MC; for welding the order is S700MC first (excellent, 85/100) then S355J2W (very good, 80/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in S355J2W and S700MC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.