Steel Q460 vs S700MC
Steel · grade comparison
Steel Q460 and S700MC are both steel grades. S700MC is the stronger of the two: yield strength 740 MPa (107 ksi) against 500 MPa (72.5 ksi) for Q460, about 48% more; tensile strength follows at 810 MPa (117 ksi) vs 620 MPa (89.9 ksi). In exchange, Q460 is the more ductile: elongation 21% versus 14% for S700MC, and S700MC is harder (245 HB vs 185 HB). Q460 runs hotter in service (350°C vs 300°C continuous) and Q460 conducts heat better (45 W/m·K vs 40 W/m·K). On the shop floor, S700MC welds better (excellent vs very good) and Q460 sits in a lower cost tier (budget, $) than S700MC (standard, $$).
Q460Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
S700MCChoose it when strength drives the design, or when it will be welded.
Q460 vs S700MC: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Hardness, Rockwell C
Same in both: Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 25%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Q460 | S700MC |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | HR | TMCP |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| HVOF Coating | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| TiAlN | Yes | — |
| TiB2 | Yes | — |
| TiCN | Yes | — |
| TiN | Yes | — |
| WC/C | Yes | — |
| ZrN | Yes | — |
Both are offered for Sheet metal. They share 22 finishes: Black Oxide, Cerakote, Chrome Plating, Copper Plating, E-Coating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Hot-Dip Galvanizing, Manganese Phosphate, Nickel Plating and 10 more.
Q460 vs S700MC — frequently asked
Is S700MC stronger than Q460?
Yes. S700MC has a typical yield strength of 740 MPa (107 ksi) against 500 MPa (72.5 ksi) for Q460 — about 48% more. Tensile strength is 810 MPa (117 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, Q460 or S700MC?
Q460 is the lower-cost material: it sits in the budget tier ($) while S700MC is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, Q460 or S700MC?
Q460, by a small margin. Both rate fair for machinability — 52/100 against 45/100 for S700MC; for welding the order is S700MC first (excellent, 85/100) then Q460 (very good, 70/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Q460 and S700MC side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.